Hydrogen Adsorption by Woodceramics Produced from Biomass

doi:10.1007/s12204-012-1280-2

Abstract

Abstract: Hydrogen adsorption characteristics of woodceramics, made from radiata pine wood fiber boards carbonized at 1 473K after impregnation with phenolic resin, with and without chemical treatment in an alkaline (KOH) or an acid (H2 SO4) solution were investigated The hydrogen adsorption capacity is improved by chemical treatment. The chemical treatment by KOH improves the adsorption capacity more than by H2SO4. The improvement of the capacity level, in any solution, is dependent on the type of chemical in the solution and its concentration. The maximum hydrogen capacity measured at 93K is mass fraction about w(H) = 2% for the woodceramics after chemical treatment in a volume fraction ? = 50% KOH solution, although that is about w(H) = 0.7% for one without chemical treatment. The microscopic condition of pores in the woodceramics is thought to vary after chemical treatment.

摘要： Hydrogen adsorption characteristics of woodceramics, made from radiata pine wood fiber boards carbonized at 1 473K after impregnation with phenolic resin, with and without chemical treatment in an alkaline (KOH) or an acid (H2 SO4) solution were investigated The hydrogen adsorption capacity is improved by chemical treatment. The chemical treatment by KOH improves the adsorption capacity more than by H2SO4. The improvement of the capacity level, in any solution, is dependent on the type of chemical in the solution and its concentration. The maximum hydrogen capacity measured at 93K is mass fraction about w(H) = 2% for the woodceramics after chemical treatment in a volume fraction ? = 50% KOH solution, although that is about w(H) = 0.7% for one without chemical treatment. The microscopic condition of pores in the woodceramics is thought to vary after chemical treatment.

CLC Number:

TB 32

TAKASAKI Akito1, IIJIMA Suguru1, YAMANE Tomoka1, OKABE Toshio2. Hydrogen Adsorption by Woodceramics Produced from Biomass[J]. Journal of shanghai Jiaotong University (Science), 2012, 17(3): 330-333.

[1]	LI Jianlin, ZHANG Zedong, LIANG Ce, ZENG Fei. Multi-Objective Robustness of Integrated Energy System Considering Source-Load Uncertainty [J]. Journal of Shanghai Jiao Tong University, 2025, 59(2): 175-185.
[2]	WANG Xinci, LIU Aiguo, WU Xiaoqu, ZHANG Yunjie. Numerical Study of Combustion Characteristics of Methane/Hydrogen Hybrid Fuel of Lean Premixed Swirl [J]. Journal of Shanghai Jiao Tong University, 2024, 58(8): 1179-1187.
[3]	FAN Hong, XING Mengqing, WANG Lankun, TIAN Shuxin. Multi-Time Scale Probabilistic Production Simulation of Wind-Solar Hydrogen Integrated Energy System Considering Hydrogen Storage [J]. Journal of Shanghai Jiao Tong University, 2024, 58(6): 881-892.
[4]	DUAN Jia’nan, XIE Jun, XING Shanxi. A Cooperative Game Allocation Strategy for Wind-Solar-Pumped Storage-Hydrogen Multi-Stakeholder Energy System [J]. Journal of Shanghai Jiao Tong University, 2024, 58(6): 872-880.
[5]	FU Wenxi, DOU Zhenlan, ZHANG Chunyan, WANG Lingling, JIANG Chuanwen, XIONG Zhan. Bi-Level Optimization Operation Method of Multi-H₂-IES Considering Dynamic Carbon Emission Factors [J]. Journal of Shanghai Jiao Tong University, 2024, 58(5): 610-623.
[6]	FAN Hong, YANG Zhongquan, XIA Shiwei. Low Carbon Economic Operation of Hydrogen-Enriched Compressed Natural Gas Integrated Energy System Considering Step Carbon Trading Mechanism [J]. Journal of Shanghai Jiao Tong University, 2024, 58(5): 624-635.
[7]	SHI Ting, JIN Ming, GE Bing, ZANG Shusheng. Forced Oscillation Characteristics of Natural Gas Mixed with Hydrogen Combustion in Gas Turbine Central Staged Burner [J]. Journal of Shanghai Jiao Tong University, 2024, 58(3): 304-311.
[8]	Yizhe Li, Yajie Li, Hao Sun, Liyao Gao, Xiangrong Jin, Yaping Li, Zhi LV, Lijun Xu, Wen Liu, Xiaoming Sun. Current Status and Perspectives of Dual-Atom Catalysts Towards Sustainable Energy Utilization [J]. Nano-Micro Letters, 2024, 16(1): 139-.
[9]	Yirong Wang, Yaohui Cheng, Chunchun Yin, Jinming Zhang, Jingxuan You, Jizheng Wang, Jinfeng Wang, Jun Zhang. Manipulating Crystal Growth and Secondary Phase PbI₂ to Enable Efficient and Stable Perovskite Solar Cells with Natural Additives [J]. Nano-Micro Letters, 2024, 16(1): 183-.
[10]	Anbin Zhou, Huirong Wang, Fengling Zhang, Xin Hu, Zhihang Song, Yi Chen, Yongxin Huang, Yanhua Cui, Yixiu Cui, Li Li, Feng Wu, Renjie Chen. Amphipathic Phenylalanine-Induced Nucleophilic-Hydrophobic Interface Toward Highly Reversible Zn Anode [J]. Nano-Micro Letters, 2024, 16(1): 164-.
[11]	Shuilin Wu, Yibing Yang, Mingzi Sun, Tian Zhang, Shaozhuan Huang, Daohong Zhang, Bolong Huang, Pengfei Wang, Wenjun Zhang. Dilute Aqueous-Aprotic Electrolyte Towards Robust Zn-Ion Hybrid Supercapacitor with High Operation Voltage and Long Lifespan [J]. Nano-Micro Letters, 2024, 16(1): 161-.
[12]	Li Ren, Yinghui Li, Zi Li, Xi Lin, Chong Lu, Wenjiang Ding, Jianxin Zou. Boosting Hydrogen Storage Performance of MgH₂ by Oxygen Vacancy-Rich H-V₂O₅ Nanosheet as an Excited H-Pump [J]. Nano-Micro Letters, 2024, 16(1): 160-.
[13]	SHEN Qi, LI Ouping, LIU Chao, CHENG Guangyuan, YU Xichong. Adaptability Analysis of Offshore New Energy Storage Technology Under Dual-carbon Background [J]. Ocean Engineering Equipment and Technology, 2024, 11(1): 106-115.
[14]	CAO Yong, JIANG Ying, XU Xiangjuan, QIAN Sicheng. Numerical Evaluation and Experimental Study on Hydrogen Induced Cracking of Subsea Super Duplex Stainless Steel Component [J]. Ocean Engineering Equipment and Technology, 2024, 11(1): 49-53.
[15]	Xiaoyu Liu, Yiming Guo, Fanghua Ning, Yuyu Liu, Siqi Shi, Qian Li, Jiujun Zhang, Shigang Lu, Jin Yi. Fundamental Understanding of Hydrogen Evolution Reaction on Zinc Anode Surface: A First-Principles Study [J]. Nano-Micro Letters, 2024, 16(1): 111-.