Novel Material of Hydrogen Generation

doi:10.1007/s12204-012-1286-9

Abstract

Abstract: A novel aluminum alloy which could react with water and generate hydrogen at room temperature was prepared via mechanical alloying (MA). The results shows that milling time, additives and mass ratio have a significant role in the hydrogen production rate. The highest hydrogen production rate of alloys reaches 95% of theoretical value. The velocity of hydrogen generation reaches more over 200mL/min for a gram alloy. Active materials (Ga and In) included in the aluminum alloys can be recycled and used repeatedly. The hydrolysis reaction between aluminum and H2O will take place and release a large amount of heat, which contributes to increasing the velocity of hydrogen generation. The reaction products consist of AlO(OH) and hydrogen.

Key words: hydrogen generation| aluminum| aluminum alloy

摘要： A novel aluminum alloy which could react with water and generate hydrogen at room temperature was prepared via mechanical alloying (MA). The results shows that milling time, additives and mass ratio have a significant role in the hydrogen production rate. The highest hydrogen production rate of alloys reaches 95% of theoretical value. The velocity of hydrogen generation reaches more over 200mL/min for a gram alloy. Active materials (Ga and In) included in the aluminum alloys can be recycled and used repeatedly. The hydrolysis reaction between aluminum and H2O will take place and release a large amount of heat, which contributes to increasing the velocity of hydrogen generation. The reaction products consist of AlO(OH) and hydrogen.

关键词: hydrogen generation| aluminum| aluminum alloy

CLC Number:

V 512

LUO Ping1 (罗平), DONG Shi-jie1 (董仕节), XIE Zhi-xiong2 (谢志雄). Novel Material of Hydrogen Generation[J]. Journal of shanghai Jiaotong University (Science), 2012, 17(3): 356-359.

References

[1] Wang H Z, Leung D Y C, Leung M K H, et al. A review on hydrogen production using aluminum and
aluminum alloys [J]. Renewable and Sustainable Energy Reviews, 2009, 13(4): 845-853.
[2] Lattin W C, Utgikar V P. Transition to hydrogen economy in the United States: A 2006 status report
[J]. International Journal of Hydrogen Energy, 2007,32(15): 3230-3237.
[3] Lu J, Fang Z Z, Sohn H Y. A hybridmethod for hydrogen storage and generation from water [J]. Journal
of Power Sources, 2007, 172: 853-858.
[4] Liu Z L, Guo B, Chan S H, et al. Pt and Ru dispersed on LiCoO2 for hydrogen generation from sodium borohydride
solutions [J]. Journal of Power Sources, 2008, 17: 6306-6311.
[5] Kojima Y, Suzuki K, Fukumoto K, et al. Hydrogen generation using sodium borohydride solution and
metal catalyst coated on metal oxide [J]. International Journal of Hydrogen Energy, 2002, 27: 1029-1034.
[6] Xu Q, Chandra M. Catalytic activities of nonnoble metals for hydrogen generation from aqueous
ammonia-borane at room temperature [J]. Journal of Hydrogen Energy, 2006, 163: 364-370.
[7] Soler L, Macanas J, Munoz M, et al. Synergistic hydrogen generation from aluminum, aluminum alloys
and sodium borohydride in aqueous solutions [J]. International Journal of Hydrogen Energy, 2007, 32:4702-4710.
[8] Fan M Q, Xu F, Sun L X. Study on the characteristic hydrolysis of milled Al-based materials for hydrogen
generation [J]. International Journal of Hydrogen Energy, 2007, 32: 2809-2815.
[9] Grosjeana M H, Zidounea M, Roue L, et al. Hydrogen production via hydrolysis reaction from ballmilled
Mg-based materials [J]. International Journal of Hydrogen Energy, 2006, 31: 109-119.
[10] Tzimas E, Filiou C, Peteves S D, et al. Hydrogen storage: State of the art and future perspective
[M]. Brussels, Belgium: European Commission, Directorate-General, Joint Research Centre, 2003.
[11] Kravchenko O V, Semeneko K N, Bulychey B M, et al. Activation of aluminum metal and its reaction
with water [J]. Journal of Alloys and Compounds, 2005, 397: 58-62.
[12] Murray J P. Aluminum production using hightemperature solar process heat [J]. Solar Energy, 1999,66(2): 133-142.

[1]	LI Yuanhui, LI Jianjun, WANG Shunchao, ZHANG Longyao, ZHU Wenfeng. Modeling and Experiment on Roll-Hemming Forming Process of Aluminum Alloy Sheet with Adhesive [J]. Journal of Shanghai Jiao Tong University, 2022, 56(4): 532-542.
[2]	ZHENG Gaoyuan, ZHAO Yixi, CUI Junhui. Formation Law of Surface Defects in Stretch-Bending Formamtion of Aluminum Trim Strip for Automobile Body [J]. Journal of Shanghai Jiao Tong University, 2022, 56(1): 53-61.
[3]	ZHOU Yu, ZHAO Yong, YU Zhongqi, ZHAO Yixi. Numerical Simulation of Stagger Spinning of Cylindrical Part with Cross Inner Ribs [J]. Journal of Shanghai Jiao Tong University, 2022, 56(1): 62-69.
[4]	HE Lihua, PAN Jianfeng, NI Jing, FENG Kai, CUI Zhi. Surface Micro-Texture and Cutting Characteristics of Milling Cutter for Die-Casting Aluminum Alloy [J]. Journal of Shanghai Jiao Tong University, 2021, 55(6): 750-756.
[5]	WANG Xianjin, GAO Xu, YU Kuigang . Fixture Locating Modelling and Optimization Research of Aluminum Alloy Sidewall in a High-Speed Train Body [J]. J Shanghai Jiaotong Univ Sci, 2020, 25(6): 706-713.
[6]	DU Huimin,LUO Zhen,AO Sansan,ZHANG Yu,HAO Zhizhuang. Influence of the Electrode Shape on Service Life in 5052 Aluminum Alloy Resistance Spot Welding [J]. Journal of Shanghai Jiaotong University, 2019, 53(6): 708-712.
[7]	DU Chenyang,KONG Qingshuai,ZHAO Yixi,YU Zhongqi. Evaluation of Flange Wrinkling Prediction Methods of Conventional Spinning for Thin-Walled Spherical Components [J]. Journal of Shanghai Jiaotong University, 2019, 53(4): 431-437.
[8]	LI Xuelong,YU Zhongqi,ZHAO Yixi,EVSYUKOV S A. Study on Flange Wrinkling Prediction in Preforming Stage During Multi-Pass Conventional Spinning [J]. Journal of Shanghai Jiaotong University, 2019, 53(11): 1375-1380.
[9]	LI Ping,ZHANG Kai,WANG Boxiaotian,XUE Kemin. Microstructure and Mechanical Properties of 7A60 Aluminum Alloy by Friction Stir Processing [J]. Journal of Shanghai Jiaotong University, 2019, 53(11): 1381-1388.
[10]	LIU Ruofan, YU Zhongqi, ZHAO Yixi, EVSYUKOV S A. Formability of Flange Constraint Spinning for Aluminum Cup Part [J]. Journal of Shanghai Jiao Tong University, 2019, 53(1): 105-110.
[11]	CHEN Weiye,ZOU Tianxia,TANG Ding,GUO Feipeng,LI Dayong. Aluminum Foil Forming Limitation Test and Numerical Simulation [J]. Journal of Shanghai Jiaotong University, 2018, 52(9): 1081-1085.
[12]	YANG Ke1,ZHAO Yixi1,FENG Changwen2,YU Zhihua2. Approach of Design of Process Dimension for Hemming of Aluminum Alloys [J]. Journal of Shanghai Jiaotong University, 2018, 52(2): 182-187.
[13]	YIN Jinpeng (尹金鹏), GAO Wenyuan* (高文元), LIU Guishan (刘贵山),HAO Hongshun (郝洪顺), YAN Shuang (闫爽), JIANG Chun* (姜淳). Gain and Noise Figure Analysis of Er³⁺-Doped YAG Transparent Ceramic Microchip Amplifier [J]. Journal of shanghai Jiaotong University (Science), 2017, 22(4): 406-410.
[14]	HUANG Zunyue，LUO Zhen，ZHANG Yu，YAO Qi. Aluminum Sheet Laser Welding Deformation Measurements [J]. Journal of Shanghai Jiaotong University, 2015, 49(03): 326-328.
[15]	SHEN Hongyuan1，2,CHEN Huabin2,LIN Tao2,CHEN Shanben2. Passive Visual Technology in Aluminum Alloy Welding [J]. Journal of Shanghai Jiaotong University, 2015, 49(03): 341-343.