车身用铝饰条拉弯成形面畸变缺陷形成规律

doi:10.16183/j.cnki.jsjtu.2020.323

摘要/Abstract

摘要：

面畸变是指零件在成形中产生的局部起伏,变截面变曲率铝饰条零件在拉弯成形过程中易产生面畸变,对整车外观质量有很大的影响,面畸变的形成机理研究对于面畸变的预防和控制具有重要的指导意义.开展了铝饰条的拉弯成形面畸变缺陷形成机理研究,进行了拉弯成形试验及面畸变测量,通过Abaqus软件平台建立了铝饰条拉弯成形仿真模型,对铝饰条零件和特征件的局部变形进行了应力应变分析,分析了面畸变形成的过程.结果表明:该类饰条类零件的截面宽度与拉弯成形弯曲半径比值大于35%时,零件产生翘曲趋势,截面形状、上模具和垫料的共同作用导致局部面畸变的产生.

关键词: 铝饰条, 面畸变, 拉弯成形, 数值模拟

Abstract:

Surface defects refer to the local undulation of the parts in the forming process. The variable cross-section and variable-curvature aluminum trim parts are prone to local surface defects during the stretch-bending process, which has a great impact on the appearance of the whole vehicle. Research on the formation mechanism of surface defects has important guiding significance for the prevention and control of surface defects. In this paper, the formation mechanism of the deformation defects of the stretch-bending forming surface of aluminum trim is studied, the stretch-bending forming test and the surface defects measurement are conducted, and the simulation model of the stretch-bending forming of aluminum trim is established by using the Abaqus software platform. In addition, the forming process of surface defects is analyzed. The results show that when the ratio of section width to bending radius is larger than 35%, the part will have a warping tendency, and the joint action of section shape, upper die, and padding will cause local surface defects.

Key words: aluminum trim, surface defects, stretch-bending forming, numerical simulation

中图分类号:

TG386

郑高媛, 赵亦希, 崔峻辉. 车身用铝饰条拉弯成形面畸变缺陷形成规律[J]. 上海交通大学学报, 2022, 56(1): 53-61.

ZHENG Gaoyuan, ZHAO Yixi, CUI Junhui. Formation Law of Surface Defects in Stretch-Bending Formamtion of Aluminum Trim Strip for Automobile Body[J]. Journal of Shanghai Jiao Tong University, 2022, 56(1): 53-61.

图/表 23

图1

图2

图3

图4

图5

图6

表1

图7

图8

图9

图10

图11

图12

图13

图14

图15

图16

图17

图18

图19

图20

图21

图22

参考文献 8

[1]	ZHANG D F, SONG K C, XU J, et al. Unified detection method of aluminium profile surface defects: Common and rare defect categories[J]. Optics and Lasers in Engineering, 2020, 126:105936. doi: 10.1016/j.optlaseng.2019.105936 URL
[2]	DE PAULSEN F, WELO T. Cross-sectional deformations of rectangular hollow sections in bending: Part II—Analytical models[J]. International Journal of Mechanical Sciences, 2001, 43(1):131-152. doi: 10.1016/S0020-7403(99)00107-1 URL
[3]	谷诤巍, 徐虹, 赵立辉, 等. 基于PS2F软件的型材拉弯成形工艺研究[J]. 电加工与模具, 2009(3):69-71.
	GU Zhengwei, XU Hong, ZHAO Lihui, et al. Research on profiles stretch bend forming process by PS2F software[J]. Electromachining & Mould, 2009(3):69-71.
[4]	GU Z W, JIA L, LI X, et al. Stretch bending defect control of L-section SUS301L stainless-steel components with variable contour curvatures[J]. Journal of Iron and Steel Research International, 2019, 26(12):1376-1384. doi: 10.1007/s42243-019-00256-4 URL
[5]	叶凌, 邹炳燕, 魏青. 钢管折弯畸变原因分析[J]. 机械设计, 2018, 35(Sup.1):267-269.
	YE Ling, ZOU Bingyan, WEI Qing. Analysis on the causes of distortion in the process of pipe bending[J]. Journal of Machine Design, 2018, 35(Sup.1):267-269.
[6]	万里翔, 刘杰, 李志超, 等. 汽车门框上条拉弯分析及截面变形评价方法[J]. 华南理工大学学报(自然科学版), 2018, 46(4):16-21.
	WAN Lixiang, LIU Jie, LI Zhichao, et al. Analytical methods for stretch and bending deformation of car door sash and evaluation of cross section shape[J]. Journal of South China University of Technology (Natural Science Edition), 2018, 46(4):16-21.
[7]	SHEN H Q, LI S H, CHEN G L. Quantitative analysis of surface deflections in the automobile exterior panel based on a curvature-deviation method[J]. Journal of Materials Processing Technology, 2012, 212(7):1548-1556. doi: 10.1016/j.jmatprotec.2012.03.005 URL
[8]	WANG H P, XU S G, CAO J. Prelimilary study on a surface distortion predictor for sheet metals: Validation in Yoshida buckling problems[C]// Institute of Virtual Manufacturing. Switzerland: Numisheet, 2008: 787-795.

截面编号	D_zj/mm
1	0.021
2	0.053
3	0.089
4	0.114
5	0.083
6	0.041
7	0.028
8	0.012

[1]	金韬, 高斌, 王强强, 周行, 何文, 冯少孔. 拟共震源高密度面波法数据反演模拟算法及应用[J]. 上海交通大学学报, 2025, 59(7): 1029-1040.
[2]	张强, 陈振华, 王文龙, 苏怀维, 迟德建. 炸点控制对钢筋混凝土T梁桥的毁伤特性数值模拟研究[J]. 空天防御, 2025, 8(5): 83-90.
[3]	王子阳 , 王晓华, 郭冲霄, 等. 串油工艺研究及方法优化[J]. 海洋工程装备与技术, 2025, 12(4): 104-115.
[4]	巩超, 侯远杭, 张宇骐, 刘殿勇, 万跃进. 畸形波浪环境下的埋首式无人艇水面运动特性[J]. 上海交通大学学报, 2025, 59(4): 447-457.
[5]	武晓龙, 夏凯龙, 孟德君, 郝晟淳, 朱铭敏. 非轴对称布局压气机试验与数值模拟研究[J]. 上海交通大学学报, 2025, 59(12): 1916-1928.
[6]	李易, 欧树彦, 梁伟栋, 董佳宝, 庄至栋. 飞行器低空大动压整流罩旋抛分离数值模拟[J]. 空天防御, 2025, 8(1): 102-108.
[7]	徐浩东, 余童真, 樊伟, 李明广, 刘念武. 顶管施工过程中浆液扩散对减阻效果影响[J]. 上海交通大学学报, 2024, 58(7): 1067-1074.
[8]	邓贺方, 夏凯龙, 滕金芳, 羌晓青, 朱铭敏, 卢少鹏. 不同转速下沟槽型机匣对跨声速压气机性能的影响[J]. J Shanghai Jiaotong Univ Sci, 2024, 29(6): 1151-1160.
[9]	刘羿伯1, 毕羽琴1, 马强2, 3, 肖华平1, 刘书海1. 水下螺旋轴流混输泵叶轮的结构设计与优化[J]. 海洋工程装备与技术, 2024, 11(4): 14-20.
[10]	冯漾漾, 丁浩亮, 胡平山, 严波. 注塑模稳态温度场的有限体积法模拟[J]. 上海交通大学学报, 2024, 58(4): 461-467.
[11]	王慧, 杜登轩, 刘海超, 喻国良, 张民曦. 均匀来流中带环翼的复合桩墩的局部冲刷数值试验研究[J]. 海洋工程装备与技术, 2024, 11(3): 1-9.
[12]	李树勋，沈恒云，刘斌才，胡迎港，马廷前. 高温熔盐止回阀受熔盐颗粒冲击的压力脉动响应[J]. J Shanghai Jiaotong Univ Sci, 2024, 29(2): 271-279.
[13]	郭同彪, 张吉, 李新亮. 压缩拐角强激波边界层干扰直接数值模拟研究[J]. 空天防御, 2024, 7(2): 29-35.
[14]	洪蕾1，肖皓1，叶佳2，马国红1. 径向超声波辅助MIG焊电弧的数值模拟[J]. J Shanghai Jiaotong Univ Sci, 2024, 29(2): 330-338.
[15]	张念凡, 肖龙飞, 陈刚. 海洋结构物波浪砰击的数值研究综述[J]. 上海交通大学学报, 2024, 58(2): 127-140.