干涉配合对复合材料机械连接结构承载能力的影响

摘要/Abstract

摘要：

综合应用试验和有限元方法，分析了不同钉孔配合下复合材料机械连接结构的拉伸强度.结果表明：在一定范围内，随着干涉量的增加，复合材料机械连接结构的承载能力提高，但是当干涉量过大时，其承载能力反而下降；连接结构的初始刚度随着干涉量的增加也呈现先增大后减小的趋势；而且，干涉配合还会影响结构的破坏模式，过大的干涉量会导致结构提前突然破坏，影响结构的安全性.通过分析受载过程中孔周的接触和纤维失效范围可知，一定的钉孔干涉可改善孔周接触情况，使得孔边载荷更加均匀，并进而提高复合材料机械连接结构的承载能力；而过大的干涉量，则可能会引起孔周大范围的纤维破坏，从而导致连接结构提前失效.

关键词: 复合材料, 干涉配合, 机械连接, 承载能力, 机理

Abstract:

The load capacity in composite mechanical joints with different fit conditions was investigated both experimentally and numerically. The analysis results show that the load capacity of composite mechanical joint structure increases at first and then decreases with the increase of the interference fit; the stiffness of the structure presents the same tendency with the interference fit increasing; the interference fit can also affect the failure mode of the composite mechanical joint and too large an interference fit can lead to a sudden failure. Adequate interference fit could improve the contact conditions around the bolt hole and result in a better load capacity of the composite joint structures.

Key words: composite, interference fit, mechanical joint, load capacity, mechanism

中图分类号:

V 258

张俊琪，刘龙权，陈昆昆，汪海. 干涉配合对复合材料机械连接结构承载能力的影响[J]. 上海交通大学学报（自然版）, 2013, 47(11): 1795-1800.

ZHANG Junqi,LIU Longquan,CHEN Kunkun,WANG Hai. Influence of Bolt-hole Interference Fit Conditions on Load Capacity in Composite Mechanical Joints[J]. Journal of Shanghai Jiaotong University, 2013, 47(11): 1795-1800.

参考文献

［1］沈真, 张晓晶. 复合材料飞机结构强度设计与验证概论［M］. 上海: 上海交通大学出版社, 2011.

［2］Cole R T, Batch E J, Potter J. Fasteners for composite structures［J］.

Composites, 1982, 13(3): 233240.

［3］魏景超, 贾普荣, 矫桂琼. 干涉对复合材料层压板连接系统的极限挤压强度影响［J］. 材料开发与应用, 2011, 26(3): 6669.

WEI Jingchao, JIA Purong, JIAO Guiqiong. An experimental study on ultimate bearing strength of composite bolt joint with interferencefit［J］. Development and Application of Material, 2011, 26(3): 6669.

［4］Lawlor V P, McCarthy M A, Stanley W F. Experimental study on effects of clearance on single bolt, single shear, composite bolted joints［J］. Plas Rubber Compos, 2002,31:405411.

［5］刘风雷, 刘丹, 刘健光. 复合材料干涉连接钉载分配研究［J］. 航空制造技术, 2011, 17: 7374.

LIU Feng, LIU Dan, LIU Jianguang. Research on pin load distribution of interferencefit composite joint［J］. Aeronautical Manufacturing Technology, 2011, 17: 7374.

［6］Binnur G K. Effect of the clearance and interferencefit on failure of the pinloaded composites［J］. Materials and Design, 2010, 31: 8593.

［7］Cao Z Q, CardewHall M. Interferencefit riveting technique in fiber composite laminates［J］. Aerospace Science and Technology, 2006, 10: 327330

［8］魏冉. 复合材料钛合金机械连接结构承载能力及钉孔配合影响研究［D］. 上海:上海交通大学航空航天学院, 2012.

［9］黄金昌，王晓冬. 复合材料夹层连接螺栓预紧力矩试验研究［J］. 飞机设计, 2009, 29(2): 3240.

HUANG Jinchang, Wang Xiaodong. Study on tightening test of joint bolt in sandwich of composites［J］. Aircraft design, 2009, 29(2): 3240.

［10］Johan E, Schon J. Effect of secondary bending on strength prediction of composite, single shear lap joints［J］. Composite Science and Technology, 2005, 65:953965.

［11］石亦平, 周玉蓉. ABAQUS有限元分析实例详解［M］. 北京: 机械工业出版社, 2011.

［12］Herrington P D, Sabbaghian M. Fators affecting the friction coefficients between matallic washers and composite surfaces［J］. Compos, 1991, 22(6): 418424.

［13］Tong L. Bearing failure of composite bolted joints with nonuniform bolttowasher clearance［J］. Composites: Part A, 2000, 31(6): 609615.

［14］Hashin Z. Failure criteria for Unidirectional fiber composite［J］. Journal of Applied Mechanics, 1980, 47: 329334.

［15］Ye L. Role of matrix resin in delamination onset and growth in composite laminates［J］. Science and Technology, 1988, 33: 257277.

［16］Camanho P P, Matthews F L. A progressive damage model for mechanically fastened joints in composite laminates［J］. Composites Part B, 2002, 33: 521529.

［17］ASTM D5961/D5961M10. Standard test method for bearing response of polymer matrix composite laminates［S］. American Society for Testing and Materials, 2010.

［18］ASTM D7248/D7248M08. Standard test method for bearing/bypass interaction response of polymer matrix composite laminates using 2fastener specimens［S］. American Society for Testing and Materials, 2008.

［19］王武, 陶华, 刘风雷, 等. 干涉配合复合材料强化机理的研究［J］. 绝缘材料, 2007, 40(1): 5154.

WANG Wu, TAO Hua, LIU Fenglei, et al. Research on the enhancement of interference_fit composite joint［J］. Insulating Materials, 2007, 40(1): 5154.

[1]	张雪, 陆云超, 韩远飞, 乐建温, 黄光法, 吕维洁. 激光增材制造非连续增强钛基复合材料组织性能调控与空天应用探索[J]. 空天防御, 2025, 8(5): 31-46.
[2]	马莎莎, 丁圣洁, 刘利民, 赵长颖, 顾汉洋, 龚帅. 高温热管碱金属工质的蒸发弯月面区域微观传热特性[J]. 上海交通大学学报, 2025, 59(5): 617-627.
[3]	贺益雄, 代永刚, 赵兴亚, 于德清, 黄立文. 河口深槽可航宽度变化水域航行决策方法[J]. 上海交通大学学报, 2025, 59(4): 489-502.
[4]	黄志迪, 高建雄, 孟令超, 程琴, 李苗苗. 考虑应力缓解效应的开孔复合材料层压板拉伸强度预测[J]. 上海交通大学学报, 2025, 59(12): 1929-1941.
[5]	叶骏, 何一冰, 李先锋, 严国灿, 燕磊. 城市电力系统演化路径的系统动力学建模分析[J]. 上海交通大学学报, 2025, 59(11): 1732-1741.
[6]	王磊, 陈哲, 王浩伟. 热处理对贮箱用原位自生铝基复合材料组织和性能的影响[J]. 空天防御, 2024, 7(6): 112-119.
[7]	陈雪, 朱龙宇, 薛钦洋, 王柯翔, 韩志林, 罗楚养. 防空导弹用树脂基复合材料研究进展[J]. 空天防御, 2024, 7(6): 76-95.
[8]	李志强, 许斌, 林楠, 王一冲, 范根莲, 谭占秋, 张荻. 高模量高强韧碳纳米管/铝合金复合材料研究进展[J]. 空天防御, 2024, 7(6): 29-37.
[9]	王进潇1, 程斌1, 2, 3, 向升1, 李思达1, 闫兴非4. 玻璃纤维复合材料胶栓混合节点在拉伸荷载下的静力与疲劳力学性能[J]. J Shanghai Jiaotong Univ Sci, 2024, 29(5): 817-830.
[10]	侯晓帆, 孙久哲, 许嘉威, 胡承儒, 付玉彬. 无机酸掺杂聚苯胺/碳纤维复合海洋电场传感器电极[J]. 上海交通大学学报, 2024, 58(3): 391-399.
[11]	徐蓉霞, 高建雄, 朱鹏年, 吴志峯. 纤维增强复合材料层压板的疲劳寿命预测方法[J]. 上海交通大学学报, 2024, 58(3): 400-410.
[12]	王贤锋, 邹凡, 刘畅, 安庆龙, 陈明. 锪窝圆角半径对CFRP/Al机械连接结构力学性能影响[J]. 上海交通大学学报, 2024, 58(3): 342-351.
[13]	程相伟, 张大旭, 杜永龙, 郭洪宝, 洪智亮. 基于X射线CT原位试验的平纹SiC_f/SiC压缩损伤演化机理[J]. 上海交通大学学报, 2024, 58(2): 232-241.
[14]	张晓玉, 周一梁, 冯冲, 姚莉丽. 船舶复合材料连接技术应用现状[J]. 海洋工程装备与技术, 2024, 11(1): 145-150.
[15]	谢敏骐, 肖慈恩, 卞嘉鹏, 刘亚坤, 范寅, 陈秀华, 刘力博. 热塑性复合材料的电弧附着特征[J]. 上海交通大学学报, 2023, 57(9): 1214-1220.