Preparation and Characterization of a New Kind of Nano-rod Shaped
Polycarboxylate Slump-Retaining Admixture Using for Concrete

doi:10.1007/s12204-012-1322-9

Abstract

Abstract: A new kind of nano-rod shaped polycarboxylic acid slump-retaining agent was synthesized. Transmission electron microscope (TEM) experiment showed that the nano-rod was bound together as macromolecular aggregates in solution. Application performance studying suggested that this kind nano-sized polymer material had excellently plasticity-retaining performance in cement-based materials and could improve endurance performance of hardened cement-based materials distinctly. The concrete with an initial slump of 2—9 cm could achieve 3 h plasticity-retaining performance with the help of this kind nano-rod. The product had extremely wide application value in the market.

Key words: nano-material| polymer| concrete| polycarboxylate| slump-retaining admixture

摘要： A new kind of nano-rod shaped polycarboxylic acid slump-retaining agent was synthesized. Transmission electron microscope (TEM) experiment showed that the nano-rod was bound together as macromolecular aggregates in solution. Application performance studying suggested that this kind nano-sized polymer material had excellently plasticity-retaining performance in cement-based materials and could improve endurance performance of hardened cement-based materials distinctly. The concrete with an initial slump of 2—9 cm could achieve 3 h plasticity-retaining performance with the help of this kind nano-rod. The product had extremely wide application value in the market.

关键词: nano-material| polymer| concrete| polycarboxylate| slump-retaining admixture

CLC Number:

TB 324

DUAN Guo-rong1,2* (段国荣), HUANG Guo-hong1,2 (黄国泓), LI Ai-mei2 (李爱梅), ZHU Ye-ran (朱烨然), GONG Ying1,2 (龚英). Preparation and Characterization of a New Kind of Nano-rod Shaped Polycarboxylate Slump-Retaining Admixture Using for Concrete[J]. Journal of shanghai Jiaotong University (Science), 2012, 17(5): 541-544.

References

[1] Flatt R J, Schober I, Raphael E, et al. Conformation of adsorbed comb copolymer dispersants [J].Langmuir, 2009, 25: 845-855.
[2] Ma B G, Wang X G, Liang W Q, et al. Study on early-age cracking of cement-based materials with superplasticizers[J]. Construction and Building Materials,2007, 21: 2017-2022.
[3] Shi H S, Kan L L. Study on the properties of chromium residue-cement matrices (CRCM) and the influences of superplasticizers on chromium (VI)-immobilising capability of cement matrices [J]. Journal of Hazardous Materials, 2009, 162: 913-919.
[4] Diamond S. The patch microstructure in concrete: The effect of superplasticizer [J]. Cement and Concrete Research, 2006, 36: 776-779.
[5] Ran Qian-ping, Tian Qian, Liu Jia-ping. The process for the cleaner production, performance and engineering applications of novel carboxylic grafted polymeric concrete slump retaining agent [J]. Journal of Basic Science and Engineering, 2003, 11(3): 304-309(in Chinese).
[6] Felekogl B, Sarikahya H. Effect of chemical structure of polycarboxylate-based superplasticizers on workability retention of self-compacting concrete [J].Construction and Building Materials, 2008, 22(9):1972-1980.
[7] Yamanda K, Takahashi T, Hanehara S, et al. Effects of the chemical structure on the properties of polycarboxylate-type superplasticizer [J]. Cement and Concrete Research, 2000, 30(2): 197-207.
[8] Li C Z, Feng N Q, Li Y D, et al. Effects of polyethlene oxide chains on the performance of polycarboxylate-type water-reducers [J]. Cement and Concrete Research, 2005, 35(5): 867-873.
[9] Borget P, Galmiche L, Meins J F, et al. Microstructural characterisation and behaviour in different salt solutions of sodium polymethacrylate-g-PEO comb copolymers [J]. Colloids and Surfaces A: Physicochemical and Engineering Aspects, 2005, 260: 173-182.

[1]	HUANG Chengjun, ZHU Tianyi, SONG Xiaobing. In-Plane Yield Criterion of Steel-Concrete-Steel Unit Panel [J]. Journal of Shanghai Jiao Tong University, 2022, 56(4): 422-430.
[2]	LIU Weihong, LIU Ye. Fast Construction of a Circuit Model for Via-Hole Transition Based on Liquid Crystal Polymer Multilayer Substrate [J]. Journal of Shanghai Jiao Tong University, 2022, 56(11): 1547-1553.
[3]	ZHANG Xiannan, LENG Yuankui, WU Weijie, LI Wanwan. Preparation and Immunoassay Application of Polyethylene Glycol Grafted Styrene Maleic Acid Copolymer Composite Microspheres [J]. Journal of Shanghai Jiao Tong University, 2021, 55(9): 1064-1070.
[4]	YANG Shuyan ∗ (杨淑雁), SONG Xiaobing (宋晓冰), JIA Hongxue (贾红学),CHEN Xi (陈溪), LIU Xila (刘西拉). Hysteretic Model for Corroded Rectangular Reinforced Concrete Bridge Column Under Seismic Loading [J]. J Shanghai Jiaotong Univ Sci, 2021, 26(6): 794-803.
[5]	BAI Xiaoyu (白晓宇), ZHENG Chen (郑晨), ZHANG Mingyi ∗ (张明义),LIU Xueying (刘雪颖), KUANG Zheng (匡政). Bond Mechanical Properties of Glass Fiber Reinforced Polymer Anti-Floating Anchor in Concrete Baseplate [J]. J Shanghai Jiaotong Univ Sci, 2021, 26(6): 804-812.
[6]	ZHAO Pengfei, XUE Xin, YANG Cheng. Simulation of Influence of End Anchorage Degradation of Stirrups Caused by Alkali Aggregate Reaction on Shear Performance of Reinforced Concrete Beams [J]. Journal of Shanghai Jiao Tong University, 2021, 55(6): 681-688.
[7]	AN Qingsheng, SUN Lidong, WU Qiusheng. Design of Carbon Fiber Reinforced Composite Launch Tube [J]. Air & Space Defense, 2021, 4(2): 13-.
[8]	ZHUANG Weimin (庄蔚敏), WANG Pengyue (王鹏跃), AO Wenhong (熬文宏), CHEN Gang (陈刚) . Experiment and Simulation of Impact Response of Woven CFRP Laminates with Different Stacking Angles [J]. J Shanghai Jiaotong Univ Sci, 2021, 26(2): 218-230.
[9]	ZHA Zhixiang, LIU Xila, XU Bo. Collapse Patterns and Their Discrimination of Reinforced Concrete Shear Wall Under Combined Stresses of Compression and Shear due to Strong Earthquake [J]. Journal of Shanghai Jiao Tong University(Science), 2020, 25(4): 495-508.
[10]	LUAN Jianze,NA Jingxin,MU Wenlong,TAN Wei,CHEN Hongli. Effect of Low Speed Loading on Failure of Aluminum Alloy-Basalt Fiber Reinforced Polymer Composite Bonded Joint [J]. Journal of Shanghai Jiaotong University, 2020, 54(11): 1200-1208.
[11]	FAN Pengxuan,CHEN Wujun,HU Jianhui,ZHAO Bing,FANG Guangqiang,CAO Zhengli,PENG Fujun. Hyper-Viscoelastic Model and Rate-Dependence in Large Strain Regime of Epoxy Shape Memory Polymer [J]. Journal of Shanghai Jiaotong University, 2019, 53(9): 1017-1022.
[12]	LIU Xiaodong,WU Lei,KONG Liang,WANG Min,CHEN Yidong. Effect of Surface and Adhesive-Bonded Properties of Carbon Fiber Reinforced Plastic/Polymer and Atmosphere Plasma Processing [J]. Journal of Shanghai Jiaotong University, 2019, 53(8): 971-977.
[13]	ZHU Maojiang,WENG Xingzhong,ZHANG Jun,YANG Bohan,LIU Junzhong. Bonding and Load Bearing Characteristics of Grouting Layer in Prefabricated Cement Concrete Pavement [J]. Journal of Shanghai Jiaotong University, 2019, 53(6): 696-703.
[14]	WANG Pu (王璞), ZHOU Dai (周岱), HUANG Zhen* (黄真). Ultimate Strength of Annular Reinforced Concrete Members Under Combined Actions [J]. Journal of Shanghai Jiao Tong University (Science), 2019, 24(4): 430-438.
[15]	ZHU Yeting,ZHU Yanfei,ZHANG Zixin,ZHUANG Qianwei,ZHENG Yifeng. Prediction and Visualization of Crack Width for the Prototype Test on Special-Shaped Shield Segments [J]. Journal of Shanghai Jiaotong University, 2019, 53(10): 1259-1268.

Preparation and Characterization of a New Kind of Nano-rod Shaped Polycarboxylate Slump-Retaining Admixture Using for Concrete

Preparation and Characterization of a New Kind of Nano-rod Shaped Polycarboxylate Slump-Retaining Admixture Using for Concrete

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments