Experimental Study of Instability Mechanism on 1 200 MPa AdvancedHigh Strength Steel Sheets in the Process of Stamping

Abstract

Abstract: The limit drawing formability of two advanced high strength steel sheets (AHSS) of tensile strength 1 200 MPa with the cup drawing test was studied. Their instability and failure mechanisms were also discussed from the standpoint of the microstructure. The results show that the limiting drawing ratio (LDR) of the DP1200 and the M1200 are 2.03 and 1.99, respectively. Their uniaxial tensile properties are difficult to accurately reflect the forming performance of material under the complex stress state. A large number of dimples on the fracture surfaces can be seen, which testifies the ductile fracture mode, but the crack propagation mechanism is not the same. For DP1200 steel, the failure mode is the crack propagation along the ferrite/martensite interfaces as well as through the martensitic grains. In M1200 steel, the crack propagates along the martensite interfaces.

Key words: advanced high strength steel sheet (AHSS), dual-phase steel, formability, fracture, propagation mechanism

CLC Number:

TG 115

HE Chang-Wei, GUO Bi-Meng, WANG Wu-Rong, WEI Xi-Cheng. Experimental Study of Instability Mechanism on 1 200 MPa AdvancedHigh Strength Steel Sheets in the Process of Stamping[J]. Journal of Shanghai Jiaotong University, 2012, 46(09): 1466-1470.

References

［1］康永林, 孙建林. 高强度薄钢板研究的新进展及其在汽车上的应用［J］. 钢铁, 2002, 37（5）：6570.
KANG Yonglin, SUN Jianlin. Development of high strength steel sheets and their application to automobile industry ［J］. Iron and Steel, 2002, 37（5）：6570.
［2］王利, 杨雄飞, 陆匠心. 汽车轻量化用高强度钢钢板的发展［J］. 钢铁, 2006, 41 (9): 18.
WANG Li, YANG Xiongfei, LU Jiangxin. Development of high strength steel shets for lightweight automobile ［J］. Iron and Steel, 2006, 41 (9): 18.
［3］苏凯, 余际星, 徐建兵. 新型汽车用高强度钢的应用现状与发展趋势［J］.钢铁钒钛,2006, 27(4):5357.
SU Kai, YU Jixing, XU Jianbing. Application and development trend of advanced high strength steel for auto ［J］. Iron Steel Vanadium Titanium, 2006, 27(4): 5357,62.
［4］乔建军, 牛枫. 1000 MPa级连续退火双相钢的组织与性能研究［J］. 热加工工艺, 2010, 39(14):158160.
QIAO Jianjun, NIU Feng. Study on microstructure and properties of continous annealing DP1000 dualphase steel［J］. Hot Working Technology, 2010, 39(14): 158160, 165.
［5］AvramovicCingara G, Ososkov Y, Jain M K, et al. Effect of martensite distribution on damage behavior in DP600 dual phase steels［J］. Materials Science and Engineering A, 2009, 516(12): 716.
［6］Sun X, Choi K S, Liu W N, et al. Predicting failure modes and ductility of dual phase steels using plastic strain localization［J］. International Journal of Plasticity, 2009, 25 (10)：18881909.
［7］Zeng D, Xia Z C, Shih H, et al. Development of shear fracture criterion for dualphase steel stamping ［EB/OL］.［20111210］. http://papers.sae.org/2009011172.
［8］金光灿, 赵征志, 徐刚, 等. 1000MPa热镀锌双相钢组织和断裂机理［J］. 北京科技大学学报, 2009, 31 (10): 12451249.
JIN Guangcan, ZHAO Zhengzhi, XU Gang, et al. Microstructure and fracture mechanism of 1000 MPa hot dip galvanized dual phase steel ［J］. Journal of University of Science and Technology Beijing, 2009, 31 (10): 12451249.
［9］梁炳文, 陈孝戴, 王志恒. 板金成形性能［M］. 北京：机械工业出版社, 1999.
［10］Baudin T, Quesne C, Jura J, et al. Microstructural characterization in a hotrolled, twophase steel［J］. Materials Characterization, 2001, 47(5): 365373.
［11］Wang Wurong, He Changwei, Zhao Zhonghua, et al. The limit drawing ratio and formability prediction of advanced high strength dualphase steels［J］. Materials and Design, 2011, 32 (6): 33203327.
［12］史刚, 王武荣, 羊军, 等. 1 000 MPa级双相钢薄板极限成形性能研究［J］. 上海交通大学学报, 2011, 45(11): 16531656.
SHI Gang, WANG Wurong, YANG Jun, et al. Study on limit formability of 1 000 MPa dual phase steel［J］. Journal of Shanghai Jiaotong University, 2011, 45(11): 16531656.

[1]	GAO Zihang (高梓航), WANG Xin (王鑫) ZHAO Yifan (赵一帆), JIN Zhehui (金哲慧), WANG Gang (王刚), GAO Shuo∗ (高硕). Piezoelectric-Based Smart Bone Plate for Fracture Healing Progress Monitoring [J]. J Shanghai Jiaotong Univ Sci, 2022, 27(4): 561-569.
[2]	YIN Yankun, YI Difei. Engineering Criticality Assessment of Key Joint for Hull Structure of Semi-Submersible Floating Production Unit [J]. Ocean Engineering Equipment and Technology, 2022, 9(1): 52-57.
[3]	ZHANG Yu, LIU Haiting, WENG Lin, SHEN Yao. Extraction of Fracture Toughness Parameters by Ring-Notched Small Punch Specimen Using Cohesive Model [J]. Journal of Shanghai Jiao Tong University, 2021, 55(7): 850-857.
[4]	GE Weiwen (葛卫文), WANG Yun (王昀), GE Kui(葛奎), WU Jiajun (吴嘉骏), FAN Jingxian (范晶娴), YANG Tianye(杨天页), WANG Qi (王齐), XU Bing (徐兵). Application of Virtual Reconstruction 3D-Printed External Fixation Helmet in Early Functional Treatment of Facial Fracture [J]. J Shanghai Jiaotong Univ Sci, 2021, 26(3): 368-371.
[5]	ZHANG Tianjia (张天嘉), JIANG Tengfei (姜腾飞), LI Biao (李彪), WANG Xudong(王旭东). Primary Clinical Research of a Patient Specific Implant System for an Old Zygomaticomaxillary Complex Comminuted Fracture [J]. J Shanghai Jiaotong Univ Sci, 2021, 26(3): 372-376.
[6]	ZHANG Cong, JIA Dejun, LI Fanchun, XU Yitong, ZHANG Yuan. Design and Simulation of a Titanium Alloy Lattice Bone Plate for 3D Printing [J]. Journal of Shanghai Jiao Tong University, 2021, 55(2): 170-178.
[7]	ZHANG Qiang, LU Zhaohui, ZHAO Ran, LUN Peiyuan. Time-Varying Reliability of Rust Cracking Model Based on Initial Defect [J]. Journal of Shanghai Jiao Tong University, 2020, 54(4): 413-420.
[8]	WANG Man (王曼), ZHANG Xiaomin (张晓敏), LONG Peng (龙鹏), JIANG Yu (蒋渝). Torsion Failure Analysis of Galvanized Steel Wires for Transmission and Distribution Lines Based on ANSYS Numerical Simulation [J]. Journal of Shanghai Jiao Tong University (Science), 2019, 24(5): 632-639.
[9]	YU Honggan,HUANG Xiaoping,ZHANG Yongkuang. Fatigue Life Prediction of a Hatch Corner Based on the Spectral Analysis and Fatigue Crack Growth Approaches [J]. Journal of Shanghai Jiaotong University, 2019, 53(2): 153-160.
[10]	LIU Ruofan, YU Zhongqi, ZHAO Yixi, EVSYUKOV S A. Formability of Flange Constraint Spinning for Aluminum Cup Part [J]. Journal of Shanghai Jiao Tong University, 2019, 53(1): 105-110.
[11]	XIAO Fenglin,ZHANG Yansong. Simulation Analysis on Fracture Modes of Ultra-High Strength Steel Spot-Welded Lap-Shear Joints [J]. Journal of Shanghai Jiaotong University, 2018, 52(3): 312-317.
[12]	HE Yuntao1,KONG Bo2,3,XI Xiaobing2,3,LUO Yun1. Design and Evaluation of a Novel Splint Used in Distal Radius Fracture [J]. Journal of Shanghai Jiaotong University, 2018, 52(2): 194-199.
[13]	WANG Xi-jie. Treatment and Analysis of Sticking Accident of an Exploration Well in Ningbo 11-1 [J]. Ocean Engineering Equipment and Technology, 2018, 5(1): 36-41.
[14]	SHEN Yongxing1,2* (沈泳星), MOLLAALI Mostafa1,2, LI Yihuan1,2 (李毅环),MA Weixin1,2 (马维馨), JIANG Jiahao3 (蒋家皓). Implementation Details for the Phase Field Approaches to Fracture [J]. Journal of Shanghai Jiao Tong University (Science), 2018, 23(1): 166-174.
[15]	DUAN Hongyan,WANG Zhiming,SANG Yuancheng. Cohesive Zone Modeling for Model III Crack Based on Near Tip Stress Field [J]. Journal of Shanghai Jiaotong University, 2017, 51(1): 113-.