凹模温度对AZ31B镁合金板材冲压成形性能的影响

doi:10.16183/j.cnki.jsjtu.2018.09.013

摘要/Abstract

摘要： 采用Nakazima半球凸模胀形法获取不同凹模温度下AZ31B镁合金板材的成形极限曲线(FLC)，研究了温冲压过程中凹模温度对镁合金板材成形性能的影响.运用有限元法对等双拉试样进行热-力耦合模拟，得到不同凹模温度下的温度场，分析AZ31B镁合金板材与凹模在热传递过程中的热-力耦合关系.另外，通过试制汽车行李箱铰链支架盖板零件，验证了实际工况下凹模温度对AZ31B镁合金板材成形极限的影响.结果表明：凹模温度的降低，会显著改变AZ31B镁合金薄板成形时的温度梯度分布，造成材料成形极限的下降以及破裂位置的改变；不同凹模温度下所得FLC的模拟值与其实验值相符.

关键词: 镁合金, 中温成形, 凹模温度, 成形极限曲线, 有限元法

Abstract: To investigate the effect of die temperature on formability of AZ31B magnesium alloy sheet in stamping, forming limit curve (FLC) of AZ31B magnesium alloy sheet was obtained through Nakazima semispherical drawing under different die temperatures. Thermo-mechanical coupling effect under heat transfer between AZ31B magnesium alloy sheet and die was analyzed based on temperature fields of biaxial tension specimens obtained by thermo-mechanical coupled simulation using finite element method. Effect of die temperature on forming limit of AZ31B alloy sheet in working condition was finally verified in a tryout stamping of hinge cover. The results show that temperature gradient distribution of AZ31B magnesium alloy is highly changed with the decline of die temperature, forming limit is thus decreased and fracture position is also affected. The FLCs under different die temperatures are proved to be in good agreement with actual stamping of AZ31B alloy sheet.

Key words: magnesium alloy, warm forming, die temperature, forming limit curve (FLC), finite element method

中图分类号:

TG 386

王紫旻，刘奇，顾瑞瑩，王武荣，韦习成. 凹模温度对AZ31B镁合金板材冲压成形性能的影响[J]. 上海交通大学学报（自然版）, 2018, 52(9): 1092-1097.

WANG Zimin,LIU Qi,GU Ruiying,WANG Wurong,WEI Xicheng. Formability of AZ31B Magnesium Alloy Sheet Under Different Die Temperatures[J]. Journal of Shanghai Jiaotong University, 2018, 52(9): 1092-1097.

参考文献

［1］高双. 冷冲压镁合金板材成型工艺及性能研究［D］. 沈阳: 沈阳工业大学机械工程学院, 2014. GAO Shuang. Research on cold stamping process and performance of magnesium alloy sheets［D］. Shen-yang: School of Mechanical Engineering, Shenyang University of Technology, 2014. ［2］刘光晓. AZ31镁合金板材高温成形极限图的理论获取［D］. 长春: 吉林大学机械工程学院, 2013. LIU Guangxiao. AZ31 magnesium alloy sheet high temperature forming limit diagram theory to obtain［D］. Changchun: School of Mechanical Engineering, Jilin University, 2013. ［3］ZHOU G, JAIN M K, WU P, et al. Experiment and crystal plasticity analysis on plastic deformation of AZ31B Mg alloy sheet under intermediate temperatures: How deformation mechanisms evolve［J］. International Journal of Plasticity, 2016, 79(4): 19-47. ［4］李文娟. AZ31B镁合金板料成形性能研究［D］. 济南: 山东大学机械工程学院, 2012. LI Wenjuan. Research on the formability of AZ31B magnesium alloy sheet［D］. Jinan: School of Mechanical Engineering, Shandong University, 2012. ［5］钟敏. AZ31镁合金板材温热成形极限及回弹研究［D］. 上海: 上海交通大学机械与动力工程学院, 2012. ZHONG Min. Research of forming limit and spring-back of magnesium alloy sheet AZ31 at warm condition［D］. Shanghai: School of Mechanical Engineering, Shanghai Jiao Tong University, 2012. ［6］BRUNI C, FORCELLESE A, GABRIELLI F, et al. Effect of temperature, strain rate and fibre orientation on the plastic flow behaviour and formability of AZ31 magnesium alloy［J］. Journal of Materials Processing Technology, 2010, 210(10): 1354-1363. ［7］ZHOU G, ANANTHAESWARA K, MITUKIEWICZ G, et al. FE simulations of gas blow forming and prediction of forming limit diagram of AZ31 magnesium sheet［J］. Journal of Materials Processing Technology, 2015, 218(4): 12-22. ［8］WANG W R, HUANG L, TAO K H, et al. Formability and numerical simulation of AZ31B magnesium alloy sheet in warm stamping process［J］. Materials & Design, 2015, 87(12): 835-844. ［9］TARI D G, WORSWICK M J. Elevated temperature constitutive behavior and simulation of warm forming of AZ31B［J］. Journal of Materials Processing Technology, 2015, 221(7): 40-55. ［10］何燕玲. 镁合金AZ31B板料胀形实验及成形性能研究［D］. 济南: 山东大学机械工程学院, 2012. HE Yanling. Magnesium alloys AZ31B sheet bulging test and the formability research［D］. Jinan: School of Mechanical Engineering, Shandong University, 2012. ［11］YOON J, LEE Y. Fracture mechanism of Mg-3Al-1Zn sheet at the biaxial state with respect to forming temperatures［J］. Materials & Design, 2014, 55(6): 43-49. ［12］WANG L F, HUANG G S, HONG-CHENG L I, et al. Influence of strain rate on microstructure and formability of AZ31B magnesium alloy sheets［J］. Transactions of Nonferrous Metals Society of China, 2013, 23(4): 916-922.

[1]	张培珍, 林芳. 开式呼吸蛙人专用氧气瓶声散射特性[J]. 上海交通大学学报, 2022, 56(6): 764-771.
[2]	张宇, 刘海亭, 翁琳, 沈耀. 环形缺口小冲杆试样结合内聚力模型提取断裂韧性参数[J]. 上海交通大学学报, 2021, 55(7): 850-857.
[3]	郑昌隆, 丁晓红, 沈洪, 赵利娟. 基于自适应成长法的舵面结构动力学拓扑优化设计方法研究[J]. 空天防御, 2021, 4(2): 7-.
[4]	王峰, 陈佳莉, 陈灯红, 范勇, 李志远, 何卫平. 基于滑动Kriging插值的EFG-SBM求解含侧边界的稳态热传导问题[J]. 上海交通大学学报, 2021, 55(11): 1483-1492.
[5]	蒋倩倩，王家序，李俊阳，肖科，唐挺，王成. 双圆弧谐波传动齿廓参数对柔轮应力影响[J]. 上海交通大学学报, 2020, 54(2): 167-175.
[6]	叶礼裕, 王超, 郭春雨, 常欣. 集中冰载工况下的桨叶边缘强度校核方法[J]. 上海交通大学学报, 2020, 54(1): 10-19.
[7]	杜慧敏，罗震，敖三三，张禹，郝志壮. 5052铝合金电阻点焊电极形状对电极寿命的影响[J]. 上海交通大学学报, 2019, 53(6): 708-712.
[8]	刘永财，鲍益东，秦雪娇，刘玉琳，陈文亮. 板料成形快速模拟的中间构形构造方法[J]. 上海交通大学学报, 2019, 53(6): 713-718.
[9]	尹雪乐，张文光，唐嘉琪，于谦. 多柄鱼骨状神经电极的微动模拟与优化设计[J]. 上海交通大学学报, 2019, 53(5): 529-534.
[10]	张向奎，王洋，王长生，胡平. 基于逆有限元法和网格映射的板材成型坯料优化[J]. 上海交通大学学报, 2019, 53(11): 1389-1394.
[11]	闫棣, 苏祺, 李四平. 屈曲问题有限元模拟的随机缺陷法[J]. 上海交通大学学报, 2019, 53(1): 19-25.
[12]	陈伟业a，邹天下a，唐鼎a，郭飞鹏a，李大永a, b. 铝箔板材成形极限试验及数值模拟[J]. 上海交通大学学报（自然版）, 2018, 52(9): 1081-1085.
[13]	应宏伟1，沈华伟1，张金红2，朱成伟1. 水位波动条件下盾构极限支护压力半解析研究[J]. 上海交通大学学报（自然版）, 2018, 52(8): 982-990.
[14]	孙双双，武丹，刘冬迪. 内嵌伪弹性形状记忆合金纤维的复合材料空心梁动态有限元分析[J]. 上海交通大学学报（自然版）, 2018, 52(7): 845-852.
[15]	段力1，高均超1，汪瑞军2，胡铭楷1，苏靖超3 成清清3，张博3，袁涛2. 航空发动机叶片表面热障涂层温度分布的仿真分析[J]. 上海交通大学学报（自然版）, 2017, 51(8): 915-920.