The hot-stamped steel with ultrahigh strength is a promising material for the fabrication of automotivecomponents. However, the coating on the sheet surface leads to a softening problem in the welded joint. Instead ofthe costly coating removal process, heat treatment is an economical and effective method for the diffusion process,which can decrease the Al concentration in the coating. In this study, a preheating treatment was carried out onAl-Si-coated 22MnB5 hot-stamped steels for the homogeneity of Al, followed by laser welding and hot stamping.The effects of the preheating on the microstructure and mechanical properties of the laser-welded joints wereinvestigated. With the preheating treatment, the Al-Si coating transformed into an Fe-Al intermetallic compoundand the difference in Al content between the coating and substrate was reduced. The Al content in the weld ofthe specimen with the preheating treatment was reduced, compared with that without the preheating treatment.The amount of δ-ferrite in the weld after laser welding was reduced largely. The distribution of long-bland-likesegregation was changed to a fine and uniform distribution. With the preheating treatment, the tensile strengthof the welded joint was significantly improved and comparable to that of the decoated joint. In conclusion, thepreheating treatment before the welding is an effective method to suppress the formation of δ-ferrite and improvethe mechanical properties of the welded joint.
WANG Qiongyan (王琼燕), LIN Wenhu (林文虎),LI Fang∗ (李芳), SHEN Chen (沈忱), HUA Xueming (华学明)
. Influence of Thermal Modification on Al-Si Coating of Hot-Stamped 22MnB5 Steel: Microstructure, Phase Transformation, and Mechanical Properties[J]. Journal of Shanghai Jiaotong University(Science), 2021
, 26(6)
: 747
-756
.
DOI: 10.1007/s12204-021-2267-7
[1] KARBASIAN H, TEKKAYA A E. A review on hot stamping [J]. Journal of Materials Processing Technology,2010, 210(15): 2103-2118.
[2] TAYLOR T, CLOUGH A. Critical review of automotive hot-stamped sheet steel from an industrial perspective[J]. Materials Science and Technology, 2018,34(7): 809-861.
[3] FAN DW, DE COOMAN B C. State-of-the-knowledge on coating systems for hot stamped parts [J]. Steel Research International, 2012, 83(5): 412-433.
[4] LIN W H, LI F, WU D S, et al. Effect of Al-Si coating on weld microstructure and properties of 22MnB5 steel joints for hot stamping [J]. Journal of Materials Engineering andPerformance,2018,27(4):1825-1836.
[5] SAHA D C, BIRO E, GERLICH A P, et al. Fusion zone microstructure evolution of fiber laser welded presshardenedsteels [J]. Scripta Materialia, 2016, 121: 18-22.
[6] VIERSTRAETE R, EHLING W, PINARD F, etal. Laser ablation for hardening laser welded steelblanks [J]. Industrial Laser Solutions for Manufacturing,2010, 25: 6-11.
[7] FLEHMIG T, GORSCHL¨UTER J, WISCHMANN S.Method and device for mechanically removing coatingsfrom coated blanks using a press and scraping knife:US9682489 [P]. 2017-06-20 [2020-09-10].
[8] LIN W H, LI F, HUA X M, et al. Effect of filler wireon laser welded blanks of Al-Si-coated 22MnB5 steel[J]. Journal of Materials Processing Technology, 2018,259: 195-205.
[9] SUN Q, DI H S, WANG X N, et al. Suppression of δ-ferrite formation on Al-Si coated press-hardened steelduring laser welding [J]. Materials Letters, 2019, 245:106-109.
[10] KANG M, KIM C, BAE S M. Laser tailor-weldedblanks for hot-press-forming steel with arc pretreatment[J]. International Journal of Automotive Technology,2015, 16(2): 279-283.
[11] FAN D W, KIM H S, OH J K, et al. Coating degradationin hot press forming [J]. ISIJ International, 2010,50(4): 561-568.
[12] MAITRA T, GUPTA S P. Intermetallic compound formationin Fe-Al-Si ternary system: Part II [J]. MaterialsCharacterization, 2002, 49(4): 293-311.
[13] GUI Z X, LIANG W K, ZHANG Y S. Enhancingductility of the Al-Si coating on hot stamping steelby controlling the Fe-Al phase transformation duringaustenitization [J]. Science China Technological Sciences,2014, 57(9): 1785-1793.
[14] SAHA D C, BIRO E, GERLICH A P, et al. Fiberlaser welding of Al-Si-coated press-hardened steel [J].Welding Journal, 2016, 95(5): 147-156.
[15] KIM C, KANG M J, PARK Y D. Laser welding of Al-Si coated hot stamping steel [J]. Procedia Engineering,2011, 10: 2226-2231.
[16] MOON J H, SEO P K, KANG C G. A study on mechanicalproperties of laser-welded blank of a boronsheet steel by laser ablation variable of Al-Si coatinglayer [J]. International Journal of Precision Engineeringand Manufacturing, 2013, 14(2): 283-288.
[17] CHEN X G, LI F, LINW H, et al. Effect of boron steelcoating on microstructure and property of laser tailorweldedblanks after hot stamping [J]. Chinese Journalof Lasers, 2017, 44(4): 115-124 (in Chinese).