Polymer-Metal Direct Molding Technology

doi:10.16183/j.cnki.jsjtu.2018.02.008

Abstract

Abstract: Polymer-metal direct forming, as a kind of forming process which combines metal and polymer directly, has a wide range of development prospects because of its combination of metal and polymer material characteristics. This paper mainly introduced the theory of polymer-metal direct molding technology and its key technology as well, summarized the latest research progress of bonding strength of compounds, and pointed out some key factors influencing the bonding strength. These lay a good foundation for the future research on bonding strength of the composite parts.

Key words: polymer-metal direct molding; bonding strength; metal surface treatment

CLC Number:

TQ 32

FAN Cong,HU Guanghong,LING Chengzhi. Polymer-Metal Direct Molding Technology[J]. Journal of Shanghai Jiao Tong University, 2018, 52(2): 176-181.

References

［1］胡广洪, 杜彦丽. 聚合物-金属组合成型及其关键技术［J］. 上海塑料, 2015(4): 6-10. HU Guanghong, DU Yanli. Polymer-to-metal hybrid technology and its key ［J］. Shanghai Plastics, 2015 (4): 6-10. ［2］GRUJICIC M, SELLAPPAN V, OMAR M A, et al. An overview of the polymer-to-metal direct-adhesion hybrid technologies for load-bearing automotive components［J］. Journal of Materials Processing Technology, 2008, 197(1-3): 363-373. ［3］MERTENS A J, SENTHILVELAN S. Effect of mating metal gear surface texture on the polymer gear surface temperature［J］. Materials Today Proceedings, 2015, 2(4/5): 1763-1769. ［4］FABRIN P A, HOIKKANEN M E, VUORINEN J E. Adhesion of thermoplastic elastomer on surface treated aluminum by injection molding［J］. Polymer Engineering & Science, 2007, 47(8): 1187-1191. ［5］KIM J Y, AHN K, JEONG S Y, et al. Enhancement of adhesion between polyphenylene sulfide and copper by surface treatments［J］. Current Applied Physics, 2014, 14(1): 118-121. ［6］OCHOA-PUTMAN C, VAIDYA U K. Mechanisms of interfacial adhesion in metal-polymer composites—Effect of chemical treatment［J］. Composites Part A: Applied Science & Manufacturing, 2011, 42(8): 906-915. ［7］KIM W S, YUN I H, LEE J J, et al. Evaluation of mechanical interlock effect on adhesion strength of polymer-metal interfaces using micro-patterned surface topography［J］. International Journal of Adhesion & Adhesives, 2010, 30(6): 408-417. ［8］YEH R Y, HSU R Q . Application of porous oxide layer in plastic/metal direct adhesion by injection molding［J］. Journal of Adhesion Science & Technology, 2015, 29(15): 1617-1627. ［9］RAMANI K, MORIARTY B. Thermoplastic bonding to metals via injection molding for macro-composite manufacture［J］. Polymer Engineering & Science, 1998, 38(5): 870-877. ［10］SALGIN B, ZKANAT , MOL J M C, et al. Role of surface oxide properties on the aluminum/epoxy interfacial bonding［J］. The Journal of Physical Chemistry C, 2013, 117(9): 4480-4487. ［11］KIM W S, KIM K H, JANG C J, et al. Micro-and nano-morphological modification of aluminum surface for adhesive bonding to polymeric composites［J］. Journal of Adhesion Science and Technology, 2013, 27(15): 1625-1640. ［12］FEISTAUER E E, GUIMARES R P M, EBEL T, et al. Ultrasonic joining: A novel direct-assembly technique for metal-composite hybrid structures［J］. Materials Letters, 2016, 170: 1-4. ［13］YEH R Y, HSU R Q. Development of ultrasonic direct joining of thermoplastic to laser structured metal［J］. International Journal of Adhesion & Adhesives, 2015, 65: 28-32. ［14］刘斌, 陈昌乾, 张步进. 金属与塑料一体化的纳米成型技术及应用［J］. 模具工业, 2015, 41(7): 1-4. LIU Bin, CHEN Changqian, ZHANG Bujin. The application of nano-moulding technology for metal and plastic’s integration ［J］. Die & Mould Industry, 2015, 41 (7): 1-4. ［15］宫清, 张雄, 张宜虎, 等. 一种金属树脂一体化成型方法和一种金属树脂复合体: CN103286910A［P］. 2013-09-11［2017-01-10］. ［16］张绍华, 雷霆, 王长明, 等. 铝或铝合金表面微纳米加工方法及铝或铝合金结构: CN103276435A［P］. 2013-09-04［2017-01-10］.

[1]	LIU Xiaodong,WU Lei,KONG Liang,WANG Min,CHEN Yidong. Effect of Surface and Adhesive-Bonded Properties of Carbon Fiber Reinforced Plastic/Polymer and Atmosphere Plasma Processing [J]. Journal of Shanghai Jiaotong University, 2019, 53(8): 971-977.
[2]	WANG Menghan,LI Yanzhao,LIU Xiao,XIA Zhizi,CHEN Mingliang. Effect of Process Parameters on Shrinkage and WarPage of Rapid Heat Cycle Molding Plastic Part [J]. Journal of Shanghai Jiaotong University, 2016, 50(02): 235-240.
[3]	XU Yuanyuan，GUI Zongyan，GAO Yun,LU Chong,CHENG Shujun. Mechanical Properties of Biodegradable Citric Acid-Based Polyester /Polylactide Blends [J]. Journal of Shanghai Jiaotong University, 2013, 47(05): 806-810.
[4]	LU Yue,RAO Ju,GONG Feirong,CHEN Jianding. Synthesis of Poly Hydroxyurethanes Based on Poly (Caprolactone) [J]. Journal of Shanghai Jiaotong University, 2013, 47(05): 827-833.
[5]	YIN Hong-Ling, SUN Mao, XU Zong-Jian, CHEN Jun. Key Technology of CAE Simulation for Large Complicated Multi-hole Plastic Part [J]. Journal of Shanghai Jiaotong University, 2012, 46(03): 504-508.
[6]	1. Institute of Bio-Inspired Structure and Surface Engineering of College of Astronautics,. Fretting Wear Characteristics of Carbon Fiber Reinforced Epoxy Resin Matrix Composites in Low Temperature [J]. Journal of Shanghai Jiao Tong University, 2018, 52(5): 604-611.