Effect of Mold Heating on High-Temperature Friction and Wear Characteristics of Uncoated 22MnB5 Boron Steel

doi:10.16183/j.cnki.jsjtu.2019.226

Abstract

Abstract:

A self-developed strip-type high-temperature friction and wear test device was used to simulate the high-temperature friction process of uncoated 22MnB5 boron steel under actual hot stamping conditions. The mold was preheated to simulate the temperature increase of the die in the hot stamping process. The effects of mold temperature on the friction behavior and mechanism of uncoated boron steel were studied by using the friction coefficient test, surface wear morphology observation, and cross-section and matrix structure chart of hot stamping boron steel. The results show that the friction coefficient between the uncoated boron steel and the H13 steel is basically stable at 0.5 when the temperature of the mold is low, and the wear mechanism is mainly classified to abrasive wear and adhesive wear. Besides, when the mold temperature exceeds 100 ℃,the friction coefficient of the uncoated boron steel decreases from 0.474 to 0.414 with an increase of temperature from 150 ℃ to 200 ℃,inferring that the adhesive wear is weakened. The Vickers hardness of the boron steel matrix is approximately close to 430 from room temperature to 100 ℃. Moreover, with the temperature further rising to 150 ℃ and 200 ℃,the hardness decreases to 413.5 and 399.7 respectively, which indicates that the mold temperature has a significant effect on the mechanical behavior of formed parts.

Key words: hot stamping, uncoated 22MnB5 steel, high-temperature friction and wear, mold heating

CLC Number:

TG115

JIANG Yihan, WU Jiasong, WANG Wurong, WEI Xicheng. Effect of Mold Heating on High-Temperature Friction and Wear Characteristics of Uncoated 22MnB5 Boron Steel[J]. Journal of Shanghai Jiao Tong University, 2021, 55(3): 258-264.

Figures/Tables 12

Fig.1

Tab.1

Fig.2

Fig.3

Fig.4

Tab.2

Fig.5

Fig.6

Fig.7

Fig.8

Fig.9

Fig.10

References 14

[1]	陈辉，景财年. 热成形技术在汽车轻量化中的应用与发展[J]. 金属热处理，2016, 41(3): 61-66.
	CHEN Hui, JING Cainian. Application and development of hot forming technology for automobile lightening[J]. Heat Treatment of Metals, 2016, 41(3): 61-66.
[2]	CASTRO M R, MONTEIRO W A, POLITANO R. Enhancements on strength of body structure due to bake hardening effect on hot stamping steel[J]. The International Journal of Advanced Manufacturing Technology, 2019, 100(1): 771-782.
[3]	郑先坤，王武荣，韦习成. 热镀锌先进高强度钢板摩擦耦合塑性变形行为[J]. 上海交通大学学报，2017, 51(4): 432-437.
	ZHENG Xiankun, WANG Wurong, WEI Xicheng. Plastic deformation behavior of hot-dipped advanced galvanized steel under the condition of friction coupling[J]. Journal of Shanghai Jiao Tong University, 2017, 51(4): 432-437.
[4]	GRACIA-ESCOSA E, GARCÍA I, DAMBORENEA J J D, et al. Friction and wear behaviour of tool steels sliding against 22MnB5 steel[J]. Journal of Materials Research and Technology, 2017, 6(3): 241-250.
[5]	张磊，赵玉璋，王武荣，等. 超高强度硼钢B1500HS的热冲压工艺试验[J]. 上海交通大学学报，2015, 49(1): 12-18.
	ZHANG Lei, ZHAO Yuzhang, WANG Wurong, et al. Experimental study of hot stamping process of B1500HS ultra high born steel[J]. Journal of Shanghai Jiao Tong University, 2015, 49(1): 12-18.
[6]	SCHWINGENSCHLÖGL P, TENNER J, MERKLEIN M. Tribological behavior of different tool steels and surface properties under hot stamping conditions[J]. Key Engineering Materials, 2018, 767: 212-219.
[7]	TIAN X W, ZHANG Y S, LI J. Investigation on tribological behavior of advanced high strength steels: Influence of hot stamping process parameters[J]. Tribology Letters, 2012, 45(3): 489-495.
[8]	GHIOTTI A, BRUSCHI S, SGARABOTTO F, et al. Tribological performances of Zn-based coating in direct hot stamping[J]. Tribology International, 2014, 78: 142-151.
[9]	HARDELL J, HERNANDEZ S, MOZGOVOY S, et al. Effect of oxide layers and near surface transformations on friction and wear during tool steel and boron steel interaction at high temperatures[J]. Wear, 2015, 330/331: 223-229.
[10]	贺斌，邓泽涵，张万鑫，等. 热冲压模具冷却水道FEM-CFD耦合优化研究[J]. 热加工工艺，2014, 43(3): 1-4.
	HE Bin, DENG Zehan, ZHANG Wanxin, et al. Optimization of cooling channels for hot stamping die based on FEM-CFD coupled method[J]. Hot Working Technology, 2014, 43(3): 1-4.
[11]	王铖，李辉平，贺连芳，等. 加热温度和模具温度对 B1500HS硼钢组织与性能的影响[J]. 金属热处理，2016, 41(10): 43-48.
	WANG Cheng, LI Huiping, HE Lianfang, et al. Effects of heating temperature and mold temperature on microstructure and properties of B1500HS boron steel[J]. Heat Treatment of Metals, 2016, 41(10): 43-48.
[12]	LIU W, LIU H S, XING Z W, et al. Effect of tool temperature and punch speed on hot stamping of ultra high strength steel[J]. Transactions of Nonferrous Metals Society of China, 2012, 22: s534-s541.
[13]	刘建国，孙书林，王玉峰. 影响热冲压制件品质的主要因素[J]. 模具制造，2016, 16(10): 31-33.
	LIU Jianguo, SUN Shulin, WANG Yufeng. Main factors of affecting the quality for hot stamping parts[J]. Die & Mould Manufacture, 2016, 16(10): 31-33.
[14]	VENTURATO G, NOVELLA M, BRUSCHI S, et al. Effects of phase transformation in hot stamping of 22MnB5 high strength steel[J]. Procedia Engineering, 2017, 183: 316-321.

材料	w/%									硬度
材料	C	Si	Mn	Cr	P	S	Mo	B	V	硬度
22MnB5	0.258	0.250	1.240	0.143	0.021	0.005	0.005	0.003	0.006	维氏硬度180
H13	0.391	0.911	0.374	5.180	0.015	0.015	1.450	0.003	0.953	洛氏硬度53.1