柠檬酸基聚酯/聚乳酸共混物的力学性能

摘要/Abstract

摘要：

通过缩聚反应制备一种可生物降解的柠檬酸基聚酯（PEGCA），采用转矩流变仪将不同反应程度的PEGCA与聚乳酸（PLA）共混，制备出一种可完全生物降解的柠檬酸基聚酯/聚乳酸共混物，考察了共混物的拉伸、冲击和弯曲性能，并采用扫描电子显微镜观察其形貌.结果表明：PEGCA对PLA的增韧效果明显，使得共混物的断裂伸长率可达316%，冲击强度提高了近7倍；在不同的应变速率下，PEGCA/PLA共混物的力学性能不同，增大应变速率，将使共混物的拉伸强度提高，断裂伸长率降低；不同反应程度的PEGCA在PLA基体中的分散性不同，低反应程度的PEGCA的分散性较差，其共混物在较高变形速率下表现出更优异的韧性和延展性.

关键词: 可生物降解, 聚乳酸, 改性, 力学性能

Abstract:

A biodegradable citric acid-based polyester (PEGCA) was synthesized by direct copolycondensation. The full biodegradable blends of PLA and PEGCA with different reaction degrees were made by using a torque rheometer. The tensile, impact and flexural properties were investigated and the morphologies of blends were assessed by scanning electron microscopy. The result shows that the PEGCA effectively improves the toughness of the blends. The elongation at break of the blends reaches 316% and the impact strength is also increased by 7 times. The tensile properties of PEGCA/PLA blends differ under different strain rate. The higher the strain rate is, the higher the tensile strength and the lower the elongation at break becomes. The dispersion of PEGCA with different reaction degrees in PLA affects the mechanical properties of the blends. The reaction degree of PEGCA affects the dispersion of PEGCA in PLA matrix. The PEGCA with low reaction degree shows relatively small dispersed phases in PLA matrix and its blend shows a better toughness and drawability under high strain rate.

Key words: biodegradable, polylactide, modification, mechanical properties

中图分类号:

TQ 323.41

徐媛媛，桂宗彦，杲云，陆冲，程树军. 柠檬酸基聚酯/聚乳酸共混物的力学性能[J]. 上海交通大学学报（自然版）, 2013, 47(05): 806-810.

XU Yuanyuan，GUI Zongyan，GAO Yun,LU Chong,CHENG Shujun. Mechanical Properties of Biodegradable Citric Acid-Based Polyester /Polylactide Blends[J]. Journal of Shanghai Jiaotong University, 2013, 47(05): 806-810.

参考文献

［1］杨斌．绿色塑料聚乳酸［M］．北京：化学工业出版社，2007: 110.

［2］Rasal R M, Janorkar A V, Hirt D E. Poly(lactic acid) modifications ［J］．Progress in Polymer Science，2010， 35（3）: 338356．

［3］饶炬，龚飞荣，陈建定，等．肝素化碳酸酯共聚物作为可降解药物支架涂层的应用［J］．上海交通大学学报，2009, 43（7）: 10761080．

RAO Ju, GONG Feirong, CHEN Jianding, et al. Heparinimmobilized copolymer of trimethylene carbonate and lactide as a biodegradable coating for drug eluting stents ［J］. Journal of Shanghai Jiaotong University, 2007, 2009， 43(7)： 10761080．

［4］Afrifah K A，Matuana L M. Impact modification of polylactide with a biodegradable ethylene/acrylate copolymer ［J］．Macromolecular Materials and Engineering, 2010, 295(9): 802811．

［5］Li B， Dong F X， Wang X L， et al. Organically modified rectorite toughened poly(lactic acid): Nanostructures, crystallization and mechanical properties ［J］. European Polymer Journal, 2009, 45（11）: 29963003．

［6］Kulinski Z, Piorkowska E. Crystallization, structure and properties of plasticized poly(Llactide) ［J］. Polymer， 2005， 46（23）： 1029010300．

［7］Sheth M，Kumar R A，Dave V，et al．Biodegradable polymer blends of poly(lactic acid) and poly(ethylene glycol) ［J］. Journal of Applied Polymer Science，1997， 66（8）： 14951505.

［8］Djordjevic I, Choudhury N R, Dutta N K, et al．Synthesis and characterization of novel citric acidbased polyester elastomers ［J］． Polymer， 2009， 50（7）： 16821691．

［9］Serrano M R，Vavra A K，Jen M，et al．Poly(diolcocitrate)s as novel elastomeric perivascular wraps for the reduction of neointimal hyperplasia ［J］．Macromolecular Bioscience， 2011， 11（5）： 700709．

［10］崔锦峰，韩培亮，郭军红，等．可生物降解弹性体聚柠檬酸乙二醇的合成与性能［J］．合成橡胶工业，2009，32（1）：2225．

CUI Jinfeng, HAN Peiliang, GUO Junhong, et al. Synthesis and properties of biodegradable poly citrateethylene glycol elastomer ［J］. China Synthetic Rubber Industry, 2009， 32(1)： 2225.

［11］Li Y，Shimizu H．Toughening of polylactide by melt blending with a biodegradable poly(ether) urethane elastomer ［J］．Macromolecular Bioscience， 2007， 7（7）：921928．

[1]	王烨成, 李洋, 张迪, 杨越, 罗震. 碳纤维增强热塑性复合材料与高强钢的电阻单元焊[J]. 上海交通大学学报, 2022, 56(10): 1349-1358.
[2]	朱强，秦飞，王武荣，韦习成. 不同搭接顺序下三层板电阻点焊接头力学性能[J]. 上海交通大学学报, 2019, 53(9): 1122-1129.
[3]	张威，敖三三，罗震，郝志壮，陈瑶，冯梦楠，解龑. 焊接能量对铝镍超声波焊接接头性能的影响[J]. 上海交通大学学报, 2019, 53(9): 1130-1135.
[4]	何冠中,楼铭,马运五,李永兵. 铝钢电阻单元焊接头力学性能模拟[J]. 上海交通大学学报, 2019, 53(5): 616-623.
[5]	祁睿格，何春霞，付菁菁，赵丽梅，姜彩昀. 无机纳米粒子对木粉/高密度聚乙烯木塑复合材料热学及力学性能的影响[J]. 上海交通大学学报（自然版）, 2019, 53(3): 373-379.
[6]	杜思琦，王继崇，彭雄奇，顾海麟. 可生物降解的黄麻纤维/聚乳酸复合材料的制备和力学性能[J]. 上海交通大学学报, 2019, 53(11): 1335-1341.
[7]	李萍，张凯，王薄笑天，薛克敏. 7A60铝合金搅拌摩擦加工组织及性能[J]. 上海交通大学学报, 2019, 53(11): 1381-1388.
[8]	俞建超，林有希. 高速加工中无氧铜的动态力学性能[J]. 上海交通大学学报（自然版）, 2018, 52(5): 587-592.
[9]	于文英，沈毓龙，徐娟，马新秀，张占先，陈世杰，周桃，刘永生. 疏水型纳米多孔SiO2减反射膜的制备及其催化机理[J]. 上海交通大学学报（自然版）, 2018, 52(12): 1634-1641.
[10]	陈建稳1，周涵1，陈务军2,赵兵2,王明洋3. 飞艇用层压织物膜材料在双向应力作用下的弹性参数分析[J]. 上海交通大学学报（自然版）, 2017, 51(3): 344-.
[11]	金雪，朱平，李晗，王庆. 防松帽搭接焊缝力学性能及分区建模方法[J]. 上海交通大学学报（自然版）, 2017, 51(11): 1297-1303.
[12]	赵君1,余海东2. 基于绝对节点坐标法的柔性双臂机构动力学分析[J]. 上海交通大学学报（自然版）, 2017, 51(10): 1160-1165.
[13]	周元敬1，徐青2，赵红霞3，高贵龙4. 壳聚糖的改性及其自由基清除性能[J]. 上海交通大学学报（自然版）, 2014, 48(11): 1613-1620.
[14]	郑钰，李宏烨，庄新村，赵震. 金属板料剪切试验方法及应用的研究现状[J]. 上海交通大学学报（自然版）, 2014, 48(03): 422-426.
[15]	张克伟1，佘欢2，刘宏亮2，疏达2，王俊2. Si含量对高强高韧7050铝合金组织和力学性能的影响[J]. 上海交通大学学报（自然版）, 2013, 47(11): 1712-1716.