考虑双模量影响的复合材料销钉连接失效分析

摘要/Abstract

摘要：

摘要：针对复合材料层压板销钉连接结构连接特性，提出一种考虑双模量影响的破坏载荷的数值模拟方法.考虑复合材料在拉伸和压缩应力状态下弹性模量的不同，根据材料所处应力条件选择适当的刚度矩阵，以三维Hashin准则作为单向复合材料层压板的失效判据，采用Camanho的刚度折减模型，将3组不同厚度和铺层的复合材料层压板破坏载荷的试验结果与考虑双模量影响和仅用拉伸模量的有限元模拟结果进行对比.结果表明，考虑双模量影响的有限元模型能够更加准确地预测最终层压板销钉连接结构的破坏载荷.

关键词: 复合材料, 双模量, 销钉连接, 渐进失效

Abstract:

Abstract： A numerical simulation method considering the effect of bimodularity was proposed for the failure analysis of pinnedjoint composite laminates. Owing to different modulus in tension and compression for composite materials, an appropriate stiffness matrix was chosen according to the stress condition. The onset of damage at each ply was predicted by 3DHashin initiation criterion together with Camanho degradation rule. Three sets of composite laminates with different thicknesses and stacking sequencees were studied. Comparison studies were conducted between experimental results and those obtained from the finite element calculations using bimodular and/or tension modulus. The results show that the finite element model considering the effect of bimodularity can more accurately predict the ultimate failure load of pinnedjoint composite laminates.

Key words: composite, bimodulus, pinjoint, progressive damage

中图分类号:

TB 332

李璇，陈秀华，史晓辉，汪海. 考虑双模量影响的复合材料销钉连接失效分析[J]. 上海交通大学学报（自然版）, 2015, 49(01): 101-108.

LI Xuan,CHEN Xiuhua,SHI Xiaohui,WANG Hai. Effect of Bimodularity on Failure Behaviors of Pinned-Joint Composite Laminates[J]. Journal of Shanghai Jiaotong University, 2015, 49(01): 101-108.

参考文献

［1］ndürücü A, Esendemir , Tunay R F. Progressive failure analysis of glassepoxy laminated compositepinnedjoints ［J］. Materials and Design, 2012, 36: 617625.

［2］Khashaba U A, Sebaey T A, Mahmoud F F, et al. Experimental and numerical analysis of pinnedjoints composite laminates: Effects of stacking sequences ［J］. Journal of Composite Materials, 2013, 47(27): 33533366.

［3］Khashaba U A, Sebaey T A, Alnefaie K A. Failure and reliability analysis of pinnedjoints composite laminates: Effects of stacking sequences ［J］. Composites Part B: Engineering, 2013, 45(1): 16941703.

［4］Esendemir . An experimental study of mechanically fastened composite joints with clearance ［J］. International Journal of Damage Mechanics, 2011, 20(3): 464480.

［5］Olmedo A, Santiuste C, Barbero E. An analytical model for predicting the stiffness and strength of pinnedjoint composite laminates ［J］. Composites Science and Technology, 2014, 90: 6773.

［6］刘斌，赵亮，徐红炉. 基于Hashin失效准则的复合材料螺栓连接损伤破坏研究［J］. 科学技术与工程, 2012, 12(8): 16711815.

LIU Bin, ZHAO Liang, XU Honglu. Failure analysis of bolted joints in composite laminates based on Hashinfailure criterion ［J］. Science Technology and Engineering, 2012, 12(8): 16711815.

［7］Leal A A, Deitzel J M, Gillespie J W. Compressive strength analysis for high performance fibers with different modulus in tension and compression ［J］. Journal of Composite Materials, 2009, 43(6): 661674.

［8］Ambartsumyan S A. The basic equations and relations of the differentmodulus theory of elasticity of an anisotropic body ［J］. Mechanics of Solids, 1969, 4(3): 4856.

［9］Bert C W. Models for fibrous composites with different properties in tension and compression ［J］. Journal of Engineering Materials and Technology, 1977, 99(4): 344349.

［10］Zinno R, Greco F. Damage evolution in bimodular laminated composites under cyclic loading ［J］. Composite Structures, 2001, 53(4): 381402.

［11］Zhang H W, Zhang L, Gao Q. An efficient computational method for mechanical analysis of bimodular structures based on parametric variational principle ［J］. Computers and Structures, 2011, 89(23): 23522360.

［12］Zhang L, Gao Q, Zhang H W. An efficient algorithm for mechanical analysis of bimodular truss and tensegrity structures ［J］. International Journal of Mechanical Sciences, 2013, 70: 5768.

［13］Hashin Z. Failure criteria for unidirectional fiber composites ［J］. Journal of Applied Mechanics, 1980, 47(2): 329334.

［14］Camanho P P, Matthews F L. A progressive damage model for mechanically fastened joints in composite laminates ［J］. Journal of Composite Materials, 1999, 33(24): 22482280.

［15］ASTM D5961/D5961M2010， Standard test method for bearing response of polymer matrix composite laminates ［S］.

[1]	王磊, 陈哲, 王浩伟. 热处理对贮箱用原位自生铝基复合材料组织和性能的影响[J]. 空天防御, 2024, 7(6): 112-119.
[2]	陈雪, 朱龙宇, 薛钦洋, 王柯翔, 韩志林, 罗楚养. 防空导弹用树脂基复合材料研究进展[J]. 空天防御, 2024, 7(6): 76-95.
[3]	李志强, 许斌, 林楠, 王一冲, 范根莲, 谭占秋, 张荻. 高模量高强韧碳纳米管/铝合金复合材料研究进展[J]. 空天防御, 2024, 7(6): 29-37.
[4]	王进潇1, 程斌1, 2, 3, 向升1, 李思达1, 闫兴非4. 玻璃纤维复合材料胶栓混合节点在拉伸荷载下的静力与疲劳力学性能[J]. J Shanghai Jiaotong Univ Sci, 2024, 29(5): 817-830.
[5]	徐蓉霞, 高建雄, 朱鹏年, 吴志峯. 纤维增强复合材料层压板的疲劳寿命预测方法[J]. 上海交通大学学报, 2024, 58(3): 400-410.
[6]	侯晓帆, 孙久哲, 许嘉威, 胡承儒, 付玉彬. 无机酸掺杂聚苯胺/碳纤维复合海洋电场传感器电极[J]. 上海交通大学学报, 2024, 58(3): 391-399.
[7]	王贤锋, 邹凡, 刘畅, 安庆龙, 陈明. 锪窝圆角半径对CFRP/Al机械连接结构力学性能影响[J]. 上海交通大学学报, 2024, 58(3): 342-351.
[8]	程相伟, 张大旭, 杜永龙, 郭洪宝, 洪智亮. 基于X射线CT原位试验的平纹SiC_f/SiC压缩损伤演化机理[J]. 上海交通大学学报, 2024, 58(2): 232-241.
[9]	张晓玉, 周一梁, 冯冲, 姚莉丽. 船舶复合材料连接技术应用现状[J]. 海洋工程装备与技术, 2024, 11(1): 145-150.
[10]	谢敏骐, 肖慈恩, 卞嘉鹏, 刘亚坤, 范寅, 陈秀华, 刘力博. 热塑性复合材料的电弧附着特征[J]. 上海交通大学学报, 2023, 57(9): 1214-1220.
[11]	李牧之, 鲍文倩, 王修成, 张一鸣, 袁昱超, 唐文勇. 复合材料护舷实船碰撞仿真方法及防护机理[J]. 上海交通大学学报, 2023, 57(6): 680-689.
[12]	薛永波a，刘钊b，李泽阳a，朱平a. 基于改进分水岭算法和U-net神经网络模型的复合材料CT图像分割方法[J]. J Shanghai Jiaotong Univ Sci, 2023, 28(6): 783-792.
[13]	刘军, 张传旭, 曲杰. 海底管道外腐蚀复合材料水下缠绕补强修复技术应用[J]. 海洋工程装备与技术, 2023, 10(4): 24-29.
[14]	高爽, 李泽邦, 李森, 初星澎, 刘晓彬, 李想. 玻璃纤维增强复合材料拉-拉疲劳研究[J]. 海洋工程装备与技术, 2023, 10(2): 57-60.
[15]	袁丽华, 梁森, 闫盛宇. 缝合平纹编织复合材料层合板的面内弹性属性[J]. J Shanghai Jiaotong Univ Sci, 2023, 28(2): 220-232.