Microstructure of Hot-Dip Galvanized Zn-Al-Mg Alloy Coating

doi:10.1007/s12204-012-1342-5

上海交通大学学报（英文版） ›› 2012, Vol. 17 ›› Issue (6): 663-667.doi: 10.1007/s12204-012-1342-5

Microstructure of Hot-Dip Galvanized Zn-Al-Mg Alloy Coating

YU Kang-cai1,2 (余康才), LI Jun2* (李俊), LIU Xin2 (刘昕), LI Jian-guo1 (李建国), XUE Xiao-huai1* (薛小怀)

(1. School of Materials Science and Engineering, Shanghai Jiaotong University, Shanghai 200240, China; 2. Baoshan Iron & Steel Co. Ltd., Shanghai 201900, China)

出版日期:2012-12-31 发布日期:2012-12-30
通讯作者: LI Jun2* (李俊),XUE Xiao-huai1* (薛小怀) E-mail:xhxue@sjtu.edu.cn, lijun@baosteel.com

Microstructure of Hot-Dip Galvanized Zn-Al-Mg Alloy Coating

YU Kang-cai1,2 (余康才), LI Jun2* (李俊), LIU Xin2 (刘昕), LI Jian-guo1 (李建国), XUE Xiao-huai1* (薛小怀)

(1. School of Materials Science and Engineering, Shanghai Jiaotong University, Shanghai 200240, China; 2. Baoshan Iron & Steel Co. Ltd., Shanghai 201900, China)

Online:2012-12-31 Published:2012-12-30
Contact: LI Jun2* (李俊),XUE Xiao-huai1* (薛小怀) E-mail:xhxue@sjtu.edu.cn, lijun@baosteel.com

摘要/Abstract

摘要： The microstructure of hot-dip galvanized Zn-11%Al-3%Mg-0.2%Si alloy coating was studied in this article. X-ray diffraction analysis revealed the coating is composed by Zn, Al andMgZn2 phase. Optical microscope (OM) and scanning electron microscope (SEM) observations showed the coating is occupied by snowflake-like dendrite, double hexagonal organization and eutectic. The coating backbone was the dendrite considered to be a phase of hexagonal close-packed (HCP) structure judging form its morphology according to the crystal growth way in the coating. Transmission electron microscopy (TEM) and energy dispersive spectroscopy (EDS) researches on the dendrite suggested that an intermediate Zn-Al phase was formed at high temperature, then decomposed into a type of Zn-Al granular eutectoid after cooling down to room temperature, while the eutectoid Zn and Al had a certain crystallographic relationship. The coating solidification process and the grain crystal structure were discussed.

关键词: hot-dip galvanized coating, Zn-Al-Mg coating, dendrites, grain orientation

Abstract: The microstructure of hot-dip galvanized Zn-11%Al-3%Mg-0.2%Si alloy coating was studied in this article. X-ray diffraction analysis revealed the coating is composed by Zn, Al andMgZn2 phase. Optical microscope (OM) and scanning electron microscope (SEM) observations showed the coating is occupied by snowflake-like dendrite, double hexagonal organization and eutectic. The coating backbone was the dendrite considered to be a phase of hexagonal close-packed (HCP) structure judging form its morphology according to the crystal growth way in the coating. Transmission electron microscopy (TEM) and energy dispersive spectroscopy (EDS) researches on the dendrite suggested that an intermediate Zn-Al phase was formed at high temperature, then decomposed into a type of Zn-Al granular eutectoid after cooling down to room temperature, while the eutectoid Zn and Al had a certain crystallographic relationship. The coating solidification process and the grain crystal structure were discussed.

Key words: hot-dip galvanized coating, Zn-Al-Mg coating, dendrites, grain orientation

中图分类号:

TG 178

YU Kang-cai1,2 (余康才), LI Jun2* (李俊), LIU Xin2 (刘昕), LI Jian-guo1 (李建国), XUE Xiao. Microstructure of Hot-Dip Galvanized Zn-Al-Mg Alloy Coating[J]. 上海交通大学学报（英文版）, 2012, 17(6): 663-667.

YU Kang-cai1,2 (余康才), LI Jun2* (李俊), LIU Xin2 (刘昕), LI Jian-guo1 (李建国), XUE Xiao-huai1* (薛小怀). Microstructure of Hot-Dip Galvanized Zn-Al-Mg Alloy Coating[J]. Journal of shanghai Jiaotong University (Science), 2012, 17(6): 663-667.

参考文献

[1] Schuerz S, Fleischanderl M, Luckeneder G H, et al. Corrosion behavior of Zn-Al-Mg coated steel sheet in sodium chloride-containing environment [J].Corrosion Science, 2009, 51(10): 2355-2363.
[2] Sch¨urz S, Luckeneder G H, Fleischanderl M, et al. Chemistry of corrosion products on Zn-Al-Mg alloy coated steel [J]. Corrosion Science, 2010, 52(10):3271-3279.
[3] Morimoto Y, Honda K, Nishimura K, et al. Excellent corrosion-resistant Zn-Al-Mg-Si alloy hot-dip galvanized steel sheet “Super Dyma” [J]. Nippon Steel Technical Report, 2003, 87(1): 24-26.
[4] Edavan R P, Kopinski R. Corrosion resistance of painted zinc alloy coated steels [J]. Corrosion Science,2009, 51(10): 2429-2442.
[5] Li Qian, Zhao Yang-zi, Luo Qun, et al. Experimental study and phase diagram calculation in Al-Zn-Mg-Si quaternary system [J]. Journal of Alloys and Compounds,2010, 501(2): 282-290.
[6] Jiang L, Volovitch P, Wolpers M, et al. Activation and inhibition of Zn-Al and Zn-Al-Mg coatings on steel by nitrate in phosphoric acid solution [J]. Corrosion Science, 2012, 60(7): 256-264.
[7] Commenda C, P¨uhringer J. Microstructural characterization and quantification of Zn-Al-Mg surface coatings [J]. Materials Characterization, 2010, 61(10):943-951.
[8] Dutta M, Halde A K, Singh S B. Morphology and properties of hot dip Zn-Mg and Zn-Mg-Al alloy coatings on steel sheet [J]. Surface and Coatings Technology,2010, 205(7): 2578-2584.
[9] Honda K, Ushioda K, Yamada W. Influence of Si addition to the coating bath on the growth of Al-Fe alloy layers in hot-dip Zn-Al-Mg alloy-coated steel sheets [J]. Iron and Steel Institute of Japan, 2011, 97(1): 19-25 (in Japanese).
[10] Klein J, Schneider J, Muske M, et al. Aluminuminduced crystallization of amorphous silicon: Influence of the aluminum layer on the process [J]. Thin Solid Films, 2004, 451-452(22): 481-484.
[11] Nomura H, Kimata Y, Kanai H. Corrosion resistance of prepainted Zn-11%Al-3%Mg-0.2%Si coated steel sheet [C]//Galvatech 2004 Conference Proceedings.Chicago, American: Local Organizing Committee,2004: 761-770.
[12] Wattiez B, Gourgues A F, Deschamps A, et al. Experimental investigation of microstructure and ageing behaviour of bulk Zn-(1-18)%Al-(0-0.06)%Mg alloys [J]. Materials Science and Engineering, 2010,A527(29-30): 7901-7911.
[13] Zhu Y H, Man H C, LeeWB. Exothermic reaction in eutectoid Zn-Al based alloys [J]. Materials Science and Engineering, 1999, A268(1-2): 147-153.
[14] Sandoval-Jimenez A, Negrete J, Torres-Villasenor G. The triclinic high temperature modification of the α phase of the Zn-Al system [J].Mater Research Bulletin, 1999, 34(14-15): 2291-2296.
[15] Sandoval-Jimenez A, Negrete J, Torres-Villasenor G. Phase transformations in the Zn-Al eutectoid alloy after quenching from the high temperature triclinic beta phase [J]. Materials Characterization, 2010, 61(11): 1286-1289.

Microstructure of Hot-Dip Galvanized Zn-Al-Mg Alloy Coating

Microstructure of Hot-Dip Galvanized Zn-Al-Mg Alloy Coating

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 1

编辑推荐

Metrics

本文评价