Durability Degradation Analysis of Raymond Cylinder Pile

Journal of Shanghai Jiaotong University ›› 2016, Vol. 50 ›› Issue (01): 158-164.

Durability Degradation Analysis of Raymond Cylinder Pile

WU Feng1,2,WANG Dongdong2,SHI Beiling2,GONG Jinghai1,FU Kun2

(1. School of Naval Architecture, Ocean and Civil Engineering, Shanghai Jiaotong University, Shanghai 200240, China; 2. Shanghai Third Harbour Engineering Science and Technology Research Institute Co. Ltd., Shanghai 200032, China)

Received:2014-11-14 Online:2016-01-29 Published:2016-01-29

Abstract

Abstract: Abstract： In this paper, the initial boundary conditions for Raymond cylinder pile durability degradation was obtained from indoor test, and status information of the durability degradation was obtained from field sampling. Field investigation and pile body sampling were made to obtain the concrete chloride ion concentration profile of large pipe piles in service for 1 to 17 years. The degradation model for Raymond cylinder pile was built by a mathematic formula of Fick’s second law. The corrosion parameters of large pipe pile, such as the chloride ion diffusion coefficient, were obtained based on the statistical analysis of large amounts of data. Concrete chloride ion penetrations of the pile body and pile cap were compared and analyzed. The durability degradation law of Raymond cylinder pile was given, providing reference for large pipe pile durability design, use and maintenance.

Key words: Raymond cylinder pile, durability degradation, field sampling, chloride ion penetration

CLC Number:

TV 33

WU Feng1,2,WANG Dongdong2,SHI Beiling2,GONG Jinghai1,FU Kun2. Durability Degradation Analysis of Raymond Cylinder Pile[J]. Journal of Shanghai Jiaotong University, 2016, 50(01): 158-164.

References

［1］潘德强. 我国海港工程混凝土结构耐久性现状及对策［J］. 华南港工, 2003(2):313. ［2］王增忠, 施建刚, 张新华. 建筑工程全寿命安全经济决策理论与应用［M］. 上海: 同济大学出版社, 2007. ［3］GUZMAN S, GALVEZ J C, SANCHO J M. Modeling of corrosioninduced cover cracking in reinforced concrete by an embedded cohesive crack finite element ［J］. Engineering Fracture Mechanics, 2012,93: 9293. ［4］MEHTA P K, BURROWS R W. Building durable structures in the 21st century［J］. Concrete International, 2001,23(3): 5763. ［5］王永东, 汤永净, 陈聪，等. 基于氯盐侵蚀的海底隧道寿命预测模型研究［J］. 结构工程师, 2012,28(4): 5761. WANG Yongdong, TANG Yongjing, CHEN Cong, et al. Study on life predicting model of subsea tunnel based on chloride corrsion［J］. Structural Engineers, 2012,28(4):5761. ［6］邵伟, 李镜培. 氯离子侵蚀钢筋混凝土管桩的使用寿命预测［J］. 同济大学学报(自然科学版), 2014,42(12): 18201825. SHAO Wei, LI Jingpei. Service life prediction of reinforced concrete pipe pile due to chloride ion corrosion［J］. Journal of Tongji University(Natural Science), 2014,42(12):18201825. ［7］ENGELLING P D, HAYDEN R F, HAWKINS R H. Raymond concrete cylinder piles in arabian gulf［C］//First International Conference on Case Histories in Geotechnical Engineering. Rolla: Missouri，1984: 249259. ［8］BROWN D D. Elba island bridge construction［J］. Foundation Facts, 1974(10):1218. ［9］BUSLOV V B, GOULD J P, KOCH R C. The precast pier［J］. Civil Engineering, 1988，58(12):4649. ［10］LEMIEUX G F. Underwater inspection of the world's longest overall bridges, part I ［J］. Concrete International,1998,20(3): 6770. ［11］中国土木工程学会. CCES012004,混凝土结构耐久性设计与施工指南（2005 年修订版）［S］. 北京: 中国建筑工业出版社, 2005. ［12］薛利俊, 陈芳斌, 杨牧,等. 不同养护方式对混凝土管桩耐久性影响的试验与分析［J］. 江苏建材, 2013(6): 2730. ［13］金伟良. 土壤与地下水环境下混凝土结构耐久性若干问题的研究［D］. 杭州：浙江大学研究生院, 2005.