Longitudinal Ultimate Strength of Composite Ship Hull Considering Delamination Damage Mode

Abstract

Abstract: Using 3D Hashin damage rules and the corresponding property degradation rules, the ultimate sagging and hogging longitudinal strength of a composite ship hull was analyzed considering the delamination damage mode based on the stress criteria of delamination. Then the degradation factor was presented which is used to predict the longitudinal strength of composite ship considering the delamination damage mode from the calculation of longitudinal strength of composite ship without considering the delamination damage model.

Key words: composite ship hull girder, 3D Hashin damage rules, property degradation, ultimate strength, delamination

CLC Number:

U661.43

ZHANG Wei-1, PU Ying-Chao-2, TANG Wen-Yong-1, ZHANG Sheng-Kun-1. Longitudinal Ultimate Strength of Composite Ship Hull Considering Delamination Damage Mode[J]. Journal of Shanghai Jiaotong University, 2012, 46(03): 394-397.

References

［1］Mouritz A P, Gellert E, Burchill P, et al. Review of advanced composite structures for naval ships and submarines［J］. Composite Structures, 2001, 53(1): 2141.
［2］Gullberg O, Olsson K A. Design and construction of GRP sandwich ship hulls［J］. Marine Structures, 1990,3(2): 93109.
［3］Smith C S. Design of submersible pressure hulls in composite materials［J］. Marine Structures, 1991, 4(2): 141182.
［4］Chirica I, Musat S D, Chirica R, et al. Torsional behaviour of the ship hull composite model［J］. Computational Materials Science, 2011,50(4): 13811386.
［5］Chen N Z, Guedes Soares C. Longitudinal strength analysis of ship hulls of composite materials under sagging moments［J］. Composite Structures, 2007, 77(1): 3644.
［6］Chen N Z, Guedes Soares C. Reliability assessment for ultimate longitudinal strength of ship hulls in composite materials［J］. Probabilistic Engineering Mechanics, 2007, 22(4): 330342.
［7］孙海虹, 陈念众, 张圣坤. 复合材料高速船极限承载能力计算与可靠性分析［J］.工程力学,2002,19(2): 124128.
SUN Haihong, CHEN Nianzhong, ZHANG Shengkun. Ultimate strength and reliability analysis of highspeed ships in composite materials［J］. Engineering Mechanics, 2002,19(2): 124128.
［8］陈建桥, 彭文杰, 魏俊红, 等. 考虑内部损伤影响的层合板最终强度预测［J］.固体力学学报，2009, 30(1): 17.
CHEN Jianqiao, PENG Wenjie, WEI Junhong, et al. Study on the laminates strength by accounting for internal damage growth［J］. Chinese Journal of Solid Mechanics， 2009,30(1) : 17.
［9］Kim R Y, Soni S R. Experimental and analytical studies on the onset of delamination in laminated composites［J］. Journal of Composite Material, 1984, 18(1): 7080.
［10］Singh S B, Ashwini Kumar. Postbukling response and strength of laminates under combined inplane loads［J］. Composites Science and Technology, 1999, 59(5): 727736.
［11］Tan S C, Perez J. Progressive failure of laminated composites with a hole under compressive loading［J］. Journal of Reinfined Plastic Composite, 1993, 12(10): 10431057.

[1]	YU Xinye, XUE Hongxiang, Yan Shuwei. Ultimate Strength and Protective Performance of Stiffened Panels Exposed to Fire-Induced High Temperature [J]. Journal of Shanghai Jiao Tong University, 2022, 56(7): 929-936.
[2]	WANG Pu (王璞), ZHOU Dai (周岱), HUANG Zhen* (黄真). Ultimate Strength of Annular Reinforced Concrete Members Under Combined Actions [J]. Journal of Shanghai Jiao Tong University (Science), 2019, 24(4): 430-438.
[3]	ZHANG Liming,LI Yuanyuan,XUE Hongxiang,TANG Wenyong. The Analysis of Ultimate Strength of Stiffened Panels Exposed to Fire Under Temperature Increase Condition [J]. Journal of Shanghai Jiaotong University, 2019, 53(12): 1420-1427.
[4]	HU Yong-ming, OUYANG Xiong. Discussions on Some Issues in Life Extension Assessment of Deep Water Jacket Structures [J]. Ocean Engineering Equipment and Technology, 2019, 6(1): 478-481.
[5]	VU Van Tuyen, YANG Ping(杨平). Tool for Predicting the Ultimate Bending Moment of Ship and Ship-Shaped Hull Girders [J]. Journal of Shanghai Jiao Tong University (Science), 2018, 23(4): 515-.
[6]	ZHU Shen,LI Siping. Numerical Simulation of Thermal Buckling of Rectangular-Shaped Delamination Bridged by Lateral Fibers in 3D Composites [J]. Journal of Shanghai Jiaotong University, 2014, 48(12): 1784-1787.
[7]	XIONG Zhixin,LUO Peilin. A Modulus Algorithm Analysis of Ultimate Strength of Pressured Hull for DeepSea Submarine [J]. Journal of Shanghai Jiaotong University, 2014, 48(04): 498-501.
[8]	ZHANG Wei, WANG Xi. Delaminated Buckling near the Surface of Piezoelectric-Piezomagnetic Laminated Shells [J]. Journal of Shanghai Jiaotong University, 2013, 47(02): 198-202.
[9]	JI Zhen-Hua, WANG De-Yu. Threshold Value of Stiffener Bending Rigidity of Transverse Densely Stiffened Plate Under Pure Shear [J]. Journal of Shanghai Jiaotong University, 2012, 46(08): 1269-1273.
[10]	DI San-Dong, ZHANG Yang, LI Si-Ping. Buckling of Rectangular Delamination Bridged by Fibers [J]. Journal of Shanghai Jiaotong University, 2011, 45(10): 1475-1478.
[11]	ZHU Bo, ZHOU Ding, LIU Wei-Qing. Analysis on Buckling Modes of Simply Supported Delaminated Beams [J]. Journal of Shanghai Jiaotong University, 2011, 45(10): 1460-1464.
[12]	SHI Guijie,WANG Deyu. Analysis of the Similar Model for Ultimate Strength Subjected to Combined Action of Bending and Torsion of a Container Ship [J]. Journal of Shanghai Jiaotong University, 2010, 44(06): 782-0786.
[13]	ZHANG Zhenxing，XIAO Gang，LI Siping . Simulation of Delamination Buckling by Fiber Bridges [J]. Journal of Shanghai Jiaotong University, 2010, 44(01): 130-0133.