Study on Limit Formability of 1 000 MPa Dual Phase Steel

Journal of Shanghai Jiaotong University ›› 2011, Vol. 45 ›› Issue (11): 1653-1656.

• Metallography and Metallurgical Technology • Previous Articles Next Articles

Study on Limit Formability of 1 000 MPa Dual Phase Steel

(1.Technical Center, SAIC Motor, Shanghai 2018041, China; 2. School of Materials Science and Engineering, Shanghai University, Shanghai 200072, China; 3. School of Naval Architecture, Ocean and Civil Engineering, Shanghai Jiaotong University, Shanghai 200240, China）

Received:2010-12-29 Online:2011-11-30 Published:2011-11-30

Abstract

Abstract: Through the cup drawing test, the onset crack and limiting drawing ratio (LDR) of 1 000 MPa dual phase (DP) steel were identified. Three yielding models: Hill, Barlat and BBC were compared in the numerical simulation. The results show that LDR of 1 000 MPa DP steel is 2.07. And Barlat yield criterion is suitable for actual test. Unlike traditional sheet materials whose crack has obvious necking, the crack mode of 1 000 MPa DP is a tensile shear fracture and cracks are on alternating 45° planes, through thickness.

Key words: dual phase steel, formability, tensile shear fracture, deep drawing

CLC Number:

TG115.5

[1]	RAN Jinyu, WANG Fengqi, YU Zhongqi, DU Chenyang, EVSYUKOV S A. Experiment of Laser Assisted Shear Spinning for Aluminum Alloy Spherical Thin-Walled Parts [J]. Journal of Shanghai Jiao Tong University, 2023, 57(10): 1337-1345.
[2]	LIU Ruofan, YU Zhongqi, ZHAO Yixi, EVSYUKOV S A. Formability of Flange Constraint Spinning for Aluminum Cup Part [J]. Journal of Shanghai Jiao Tong University, 2019, 53(1): 105-110.
[3]	HE Chunfeng,ZHAO Yixi,HUANG Sheng. Microstructural Study of Advanced High Strength Dual-Phase Steels Sheet Under Stretch-Bending Forming Process [J]. Journal of Shanghai Jiaotong University, 2014, 48(05): 618-623.
[4]	WEN Tong (温彤), GAO Rui (郜瑞), CHEN Xia (陈霞). Influence of High Frequency Vibration on Deep Drawing Process of AZ31 Sheet at Room Temperature [J]. Journal of shanghai Jiaotong University (Science), 2012, 17(4): 456-460.
[5]	HE Chang-Wei, GUO Bi-Meng, WANG Wu-Rong, WEI Xi-Cheng. Experimental Study of Instability Mechanism on 1 200 MPa AdvancedHigh Strength Steel Sheets in the Process of Stamping [J]. Journal of Shanghai Jiaotong University, 2012, 46(09): 1466-1470.
[6]	Zhao X.; Chang H.; Tang B.; Zhang X.-H.; Kou H.-C.; Li J.-S.. Numerical analysis of material properties in deformation of near hemispherical shells [J]. J Shanghai Jiaotong Univ Sci, 2011, 16(2): 209-213.
[7]	NIU Jianhuia，ZHU Pinga，b，GUO Yongjina . Mechanical Properties of Hotdip Galvanized Dual Phase Steel DP590 and Its Constitutive Model [J]. Journal of Shanghai Jiaotong University, 2010, 44(10): 1382-1387.

Study on Limit Formability of 1 000 MPa Dual Phase Steel

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 7

Recommended Articles

Metrics

Comments