三层钢板胶焊熔核形成过程的有限元分析

沈洁1，张延松2   

  1. 1. 上海海洋大学 工程学院， 上海 201300； 2. 上海交通大学 机械与动力工程学院，上海 200240
  • 出版日期:2019-06-28 发布日期:2019-07-23
  • 作者简介:沈洁（1983-），男，上海市人，讲师，主要从事多层板点焊的数值模拟及质量控制. 电话（Tel.）:021-61900836；E-mail: j-shen@shou.edu.cn.
  • 基金资助:
    上海高校青年教师培养计划（ZZHY15010），上海海洋大学博士启动基金项目（A2-0203-00-100341）

Finite Element Analysis of Weld Nugget Formation in Weld-Bonding of Three Stacks of Steel Sheets

SHEN Jie1,ZHANG Yansong2   

  1. 1. College of Engineering Science and Technology, Shanghai Ocean University, Shanghai 201300, China; 2. School of Mechanical Engineering, Shanghai Jiao Tong University, Shanghai 200240, China
  • Online:2019-06-28 Published:2019-07-23

PDF (PC)

259

摘要： 基于ANSYS有限元分析软件，将胶层引起的钢板间接触电阻进行参数化处理，建立了考虑胶层作用的三层钢板胶焊熔核形成过程的多物理场耦合模型，从结构场、电场、温度场分布等方面分析三层钢板胶焊熔核的形成特点，并通过实验验证了所建模型的可靠性.结果表明：对于厚度为 0.8mm DC04低碳钢、厚度 1.4mm DP600双相钢和厚度 1.8mm DP780双相钢的三层钢板胶焊，胶层使得相同电流下三层钢板胶焊熔核的形成时刻比无胶层的点焊熔核的形成时刻提前了约 40ms；在DP600双相钢与DP780双相钢接触面的熔核形成时刻比在DC04低碳钢与DP600双相钢接触面的熔核形成时刻提前约80ms.

关键词: 三层钢板； 胶焊； 熔核形成； 有限元分析

Abstract: Based on the ANSYS software, a multi-physics finite element model was established to research the weld nugget formation during the weld-bonding process of three stacks of steel sheets. The contact resistance between the steel sheets with the adhesive was parameterized in this model to illustrate the effect of the adhesive on the weld-bonding process. The calculation results in the structure, electric and thermal field during the weld nugget formation were investigated and validated by the experiment. The research results show that the weld nugget formation in the weld-bonding joint with 0.8mm DC04, 1.4mm DP600 and 1.8mm DP780 is about 40ms earlier than that in the resistance spot welding joint under the same welding condition. The weld nugget formation between DP600 and DP780 is 80 ms earlier than that between DC04 and DP600 during the weld-bonding process.

Key words: three stacks of steel sheets; weld-bonding; weld nugget formation; finite element analysis