摘要/Abstract

摘要：

基于光谱学理论分析氩原子谱线波长为794.8 nm的特征谱发射系数、连续谱发射系数和总发射系数与温度之间的关系，以及连续谱对标准温度法的影响，并对标准温度法的曲线进行修正；利用具有高速摄影的电弧光谱采集系统拍摄氩原子波长为794.8 nm的特征谱的电弧图像；根据修正后的标准温度法计算直流钨极惰性气体保护焊的电弧温度场分布，对修正前、后的电弧温度场加以比较.结果表明，考虑连续谱时，电弧的温度有所升高.结合光谱仪拍摄的电弧谱线强度分布规律表明，连续谱对氩原子波长为794.8 nm的特征谱的温度计算结果影响较小.

关键词: 钨极惰性气体保护焊, 电弧温度场, 标准温度法, 连续谱

Abstract:

In order to improve the accuracy of measurement by arc image obtained by high speed camera, the modified Fowler-Milne method based on continuum spectrum was used. Based on the theory of spectrum, the relationships between emission coefficient and temperature were calculated. The emission coefficient includes spectrum line, continuum spectrum and total emission coefficient for 794.8 nm. The influence of continuum spectrum for FowlerMilne method was analyzed, and then the Fowler-Milne method was modified, arc image of spectra line in 794.8 nm was captured by high speed camera. The temperature distribution of direct current-tungsten intert gas arc welding was calculated according to the modified FowlerMilne method. Arc temperature field was compared before and after modification. The temperature field increases when continuum spectrum is taken into account. The result of spectrometer proves that the influence of continuum spectrum is small.

Key words: tungsten intert gas arc (TIG) welding, arc temperature field, FowlerMilne method, continuum spectrum

中图分类号:

TG 403

肖笑，华学明，李芳，吴毅雄. 基于连续谱修正的标准温度法的钨极惰性气体保护焊电弧温度场分析[J]. 上海交通大学学报（自然版）, 2013, 47(05): 766-769.

XIAO Xiao,HUA Xueming,LI Fang,WU Yixiong. Analysis on Temperature of TIG Welding Based on Continuum Spectrum for Modified Fowler-Milne Method[J]. Journal of Shanghai Jiaotong University, 2013, 47(05): 766-769.

参考文献

［11］Ma S, Gao H, Wu L. Modified FowlerMilne method for the spectroscopic determination of thermal plasma temperature without the measurement of continuum radiation［J］. Review of Scientific Instruments, 2011, 82(1): 01310418.

［1］Gick A E F, Quigeky M B C, Richards P H. The use of electrostatic probes to measure the temperature profiles of welding arcs［J］. J Phys D: Appl Phys, 1973, 6(16): 19421950.

［2］Murphy A B, Farmer A J D. Temperature measurement in thermal plasmas by Rayleigh scattering［J］. J Phys D: Appl Phys, 1992, 25(4): 634643.

［3］Tanaka M, Tashiro S. Electron temperature measurement of tungsten inert gas arcs［J］. Thin Solid Films, 2008, 516(19): 66286633.

［4］Haddad G N, Farmer A J D. Temperature determinations in a freeburning arc. I. Experimental techniques and results in argon［J］. J Phys D: Appl Phys, 1984, 17(6): 11891196.

［5］Olsen H N. Thermal and electrical properties of an argon plasma［J］. Physics of Fluids, 1959, 2(6): 614623.

［6］Sawato H, Tashiro S, Nakata K, et al. Measurement of dynamical variation in twodimensional temperature distribution of TIG pulsedarcs［J］. Transactions of JWRI, 2010, 39(2): 193194.

［7］Thornton M F. Spectroscopic determination of temperature distributions for a TIG arc［J］. J Phys D: Appl Phys, 1993, 26(9): 14321439.

［8］Maouhoub E, Coitout H, Parizet M. Excitation temperature measurements in an argonCO2 thermal plasma［J］. IEEE Transactions on Plasma Science, 1999, 27(5): 14691475.

［9］顾小燕. 电弧等离子体辐射在焊接过程检测上的应用研究［D］. 太原:中北大学材料学院， 2009.

［10］Ma S, Gao H, Wu L. Spatial spectroscopic diagnostics of arc plasmas by monochromatic imaging［J］. IEEE Transaction on Plasma Science, 2008, 36(4): 10541055.

［12］Ma S, Gao H, Wu L. Time resolved characterization of a freeburning argon arc after ignition by optical emission spectroscopy［J］. Journal of Applied Physics, 2011, 110(2): 02610213.

［13］Ma S, Gao H, Zheng S, et al. Spectroscopic measurement of temperatures in pulsed TIG welding arcs［J］. Journal of Physics D: Applied Physics, 2011, 44(40): 405202112.

［14］过增元, 赵文华. 电弧和热等离子体［M］. 北京: 科学出版社, 1986.

［15］Iordanova E, De Vries N, Guillemier M, et al. Absolute measurements of the continuum radiation to determine the electron density in a microwaveinduced argon plasma［J］. Journal of Physics D: Applied Physics, 2008, 41(1): 01520818.

［16］Wilbers A T M, Kroesen G M W, Timmermans C J, et al. The continuum emission of an arc plasma［J］. Journal of Quantitative Spectroscopy and Radiative Transfer, 1991, 45(1): 110.

［17］Beulens J J, De Graaf M J, Schram D C. Axial temperatures and electron densities in a flowing cascaded arc: model versus experiment［J］. Plasma Sources Science and Technology, 1993, 2(3): 180189.

[1]	张刚, 樊丁, 石玗, 顾玉芬, 朱明, 闫培民. 钨极惰性气体保护焊焊枪运动姿态的传感与验证[J]. 上海交通大学学报, 2016, 50(10): 1559-1563.
[2]	石玗, 王雪宙, 朱明, 张刚, 樊丁. 手工钨极惰性气体保护焊焊枪姿态的三维传感与分析[J]. 上海交通大学学报, 2016, 50(10): 1555-1558.
[3]	李春凯, 石玗, 朱明, 杜雷明, 顾玉芬. 不同标定窗口条件下的连续焊接熔池振荡频率检测与分析[J]. 上海交通大学学报, 2016, 50(10): 1550-1554.
[4]	朱加雷, 王纪兵, 焦向东, 瞿怀宇, 郭怀书. 脉动送丝频率和抽丝距离对铝焊接过程中气孔去除效果的影响[J]. 上海交通大学学报, 2016, 50(10): 1627-1630.
[5]	周凯荣, 陈建, 陈玉喜, 陈华斌, 陈善本. 基于原位测量的钨极惰性气体保护焊焊接过程高温应变表征与计算[J]. 上海交通大学学报, 2016, 50(10): 1588-1591.
[6]	梁明龙, 周凯荣, 倪加明, 马宏波, 陈善本, 陈华斌. 2219铝合金变极性钨极惰性气体保护焊的焊缝成形模糊控制系统[J]. 上海交通大学学报, 2016, 50(10): 1583-1587.
[7]	张刚，石玗，李春凯，樊丁，黄健康. 钨极惰性气体保护焊熔池三维自由表面特征参数的激光视觉测量[J]. 上海交通大学学报（自然版）, 2015, 49(03): 301-305.