热镀锌先进高强度钢板摩擦耦合塑性变形行为

摘要/Abstract

摘要：

采用自行研制的板带式耦合摩擦试验机，通过设置不同的下压量和载荷的组合获得摩擦过程中钢板的不同塑性变形量，以此来模拟实际冲压过程中在成形力作用下不同变形量板料与模具的相对滑动.通过比较3种不同变形量下的表面粗糙度、摩擦系数和动态演化过程来确定模具拉毛的萌生，研究了塑性变形量对拉毛磨损的影响规律.结果表明：在耦合变形的摩擦条件下，拉毛萌生一般会经历“锌层开裂”、“材料转移”、“积聚长大”3个阶段；而塑性变形量越大，拉毛萌生越早，板材损伤越严重；拉毛产生的表面损伤是黏着磨损和犁沟效应共同作用的结果.

关键词: 高强度钢, 耦合摩擦, 塑性变形, 拉毛

Abstract:

Different plastic deformation under the condition of friction coupling on a selfdeveloped friction tester was obtained by setting the reduction of punch and load. The friction tester can simulate the relative sliding under the forming force in the process of practical stamping. The surface roughness, friction coefficient and dynamic evolution were studied and analyzed to determine galling initiation. The results show that the galling initiation would go through three stages of film cracking, transfer and agglomerate, and the galling initiated earlier as the plastic deformation was larger. The surface damage was resulted from the effect of adhesive wear and plowing.

Key words: high strength steel, friction coupling, plastic deformation, galling

中图分类号:

TG 386

郑先坤，王武荣，韦习成. 热镀锌先进高强度钢板摩擦耦合塑性变形行为[J]. 上海交通大学学报（自然版）, 2017, 51(4): 432-.

ZHENG Xiankun,WANG Wurong,WEI Xicheng. Plastic Deformation Behavior of HotDipped Advanced Galvanized Steel#br# Under the Condition of Friction Coupling[J]. Journal of Shanghai Jiaotong University, 2017, 51(4): 432-.

参考文献

［1］GRD A, KRAKHMALEV P, BERGSTRM J. Influence of tool steel microstructure on origin of galling initiation and wear mechanisms under dry sliding against a carbon steel sheet［J］. Wear, 2009, 267(1): 387393.
［2］HEIDE E V D, SCHIPPER D J. Galling initiation due to frictional heating［J］. Wear, 2003, 254(11): 11271133.
［3］CARLSSON P, BEXELL U, OLSSON M. Tribological performance of thin organic permanent coatings deposited on 55%AlZn coated steel: Influence of coating composition and thickness on friction and wear［J］. Wear, 2001, 251(1): 10751084.
［4］JEON J, BRAMLEY A N. A friction model for microforming［J］. The International Journal of Advanced Manufacturing Technology, 2007, 33(1/2): 125129.
［5］HUMMEL S R. An application of frictional criteria for determining galling thresholds in line contact tests［J］. Tribology International, 2002, 35(12): 801807.
［6］KIM H, SUNG J, GOODWIN F E, et al. Investigation of galling in forming galvanized advanced high strength steels (AHSSs) using the twist compression test (TCT)［J］. Journal of Materials Processing Technology, 2008, 205(1): 459468.
［7］ASTM International. ASTM G4015 standard terminology relating to wear and erosion ［EB/OL］. (20150106) ［20150910］. https://www.astm.org/Standards/G40.htm.
［8］WANG W R, WANG K, ZHAO Y Z, et al. A study on galling initiation in friction coupling stretch bending with advanced high strength hotdip galvanized sheet ［J］. Wear, 2015, 328/329: 286294
［9］GEARING B P, MOON H S, ANAND L. A plasticity model for interface friction: Application to sheet metal forming［J］. International Journal of Plasticity, 2001, 17(2): 237271
［10］孙胜伟. 轿车车身覆盖件冲压拉毛问题分析及对策［J］. 汽车工艺与材料, 2012 (12): 14.
SUN Shengwei. Analysis and countermeasure for galling in the stamping of car body panels［J］. Automobile Technology and Material, 2012 (12): 14.
［11］鲍平, 蒋浩民, 陈新平. 热镀锌铁合金钢板冲压成形过程表面特性研究［J］. 锻压装备与制造技术, 2008, 42(3): 7374.
BAO Ping, JIANG Haomin, CHEN Xinping. Surface evolution of zinccoated galvanized steel in the stamping process［J］. China Metalforming Equipment and Manufacturing Technology, 2008, 42(3): 7374.
［12］WANG W R, HUA M, WEI X C. A comparison study of sliding friction behavior between two high strength DP590 steel sheets against heat treated DC53 punch: Hotdip galvanized sheet versus cold rolled bare sheet［J］. Tribology International, 2012, 54: 114122.

[1]	谢鹏, 刘昊, 杨清书. 脐带缆超双相不锈钢管的受力分析[J]. 海洋工程装备与技术, 2018, 5(增刊): 60-64.
[2]	王志坚，陈晓阳，沈雪瑾. 考虑粗糙峰弹塑性变形和润滑油性质的有限长线接触副混合润滑模型[J]. 上海交通大学学报（自然版）, 2018, 52(5): 525-532.
[3]	肖凤琳，张延松. 超高强度钢电阻点焊拉剪接头断裂模式的模拟分析[J]. 上海交通大学学报（自然版）, 2018, 52(3): 312-317.
[4]	顾新建，于忠奇，宋洋. 工艺参数对高强度钢冷冲压界面温度影响分析[J]. 上海交通大学学报（自然版）, 2017, 51(4): 426-.
[5]	彭雪锋1，韩静涛1，刘靖1，晏培杰2. 感应回火对冷成形高强度钢方管力学特性的影响[J]. 上海交通大学学报（自然版）, 2017, 51(4): 438-.
[6]	晏佳伟，胡启，王振振，陈军. 不同硬化模型对第3代超高强度钢板冲压回弹预测的比较[J]. 上海交通大学学报（自然版）, 2017, 51(11): 1334-1339.
[7]	丁亚男，谭淑霖，韩先洪，崔振山. 硼钢热冲压产品的力学性能预测模型及U型件验证[J]. 上海交通大学学报（自然版）, 2017, 51(11): 1320-1327.
[8]	段红燕,王智明,桑元成. III型裂纹裂尖应力场的内聚力模型[J]. 上海交通大学学报（自然版）, 2017, 51(1): 113-.
[9]	阎昱，王海波，赵溦. 与应变速率相关的DP980高强度钢板辊弯成形的本构模型建立[J]. 上海交通大学学报（自然版）, 2015, 49(01): 7-11.
[10]	晁灿1，赵亦希1，康稳1，晏培杰2，马跃峰2. QSTE700型冷弯高强度钢方管的冷作硬化效应[J]. 上海交通大学学报（自然版）, 2014, 48(05): 605-609.
[11]	何昌炜, 郭必檬, 王武荣, 韦习成. 1 200 MPa级超高强度钢板冲压成形性能及其断裂机理的实验研究[J]. 上海交通大学学报（自然版）, 2012, 46(09): 1466-1470.
[12]	汤禹成,徐栋恺,陈军. 高强度钢板复杂零件的冲压压边圈拓扑优化[J]. 上海交通大学学报（自然版）, 2010, 44(01): 6-0010.