690合金传热管疲劳裂纹扩展研究

摘要/Abstract

摘要：

摘要：采用销加载拉伸方法和直流电压降法测试技术，测量了室温和高温325 ℃空气中3种不同工艺的690合金传热管的疲劳裂纹扩展速率.试验采用ParisErdogan公式进行拟合分析，证明了结果的真实性和可靠性.高温加速了疲劳裂纹扩展.由疲劳裂纹扩展速率曲线可以预测出3种690管材在高温325 ℃下的门槛应力强度因子幅值ΔKth，扫描电子显微镜下观察断口形貌，疲劳裂纹的扩展为穿晶形式，在穿晶断口上观察到明显的疲劳辉纹和微塑性区.

关键词: , 690合金, 疲劳裂纹扩展速率, 销加载拉伸, 直流电压降

Abstract:

Abstract： Fatigue crack growth rate (FCGR) data of three kinds of alloy 690 by different manufacturing process were generated in air at room temperature and 325 ℃ using the pin-loading tension (PLT) specimen and direct current potential drop (DCPD) method. The testing data were modeled with the Paris-Erdogan equation, and a linear relation between log(da/dt) and log(ΔK) was observed, which indicated good veracity and reliability of results. The threshold stress intensity factor amplitude ΔKth of the three alloys was predicted from the fatigue crack growth curve at 325 ℃, and material B has the highest ΔKth, showing best fatigue resistance performance. Scanning electron microscopy (SEM) examination of the fatigue fracture surfaces revealed transgranular attack, and the transgranular regions of the fatigue fracture surface were covered with striationlike features, indicative of micro-plastic deformantion.

Key words: alloy 690, fatigue crack growth rate, pin-loading tension, direct current potential drop

中图分类号:

TL 341

陈凯1，杜东海1，陆辉1，张乐福1，石秀强2，徐雪莲2. 690合金传热管疲劳裂纹扩展研究[J]. 上海交通大学学报（自然版）, 2014, 48(11): 1639-1643.

CHEN Kai 1，DU Donghai1，LU Hui1，ZHANG Lefu1,SHI Xiuqiang2，XU Xuelian2. Fatigue Crack Growth of Alloy 690 Tubing[J]. Journal of Shanghai Jiaotong University, 2014, 48(11): 1639-1643.

参考文献

［1］Young B A, Gao X, Srivatsan T S, et al. An investigation of the fatigue crack growth behavior of INCONEL 690［J］. Materials Science and Engineering: A, 2006, 416(1): 187191.

［2］Li X, Wang J, Han E H, et al. Corrosion behavior for Alloy 690 and Alloy 800 tubes in simulated primary water［J］. Corrosion Science, 2013, 67: 169178.

［3］Chai G, Liu P, Zhou N, et al. Low and high cycle fatigue behavior of nickelbase alloy at high temperatures［J］. Procedia Engineering, 2013, 55: 671676.

［4］MacDonald P E, Shah V N, Ward L W, et al. Steam generator tube failures［R］. Nuclear Regulatory Commission, Washington, DC (United States). Div. of Safety Programs; Idaho National Engineering Lab., Idaho Falls, ID (United States), 1996.

［5］AlRubaie K S, Godefroid L B, Lopes J A M. Statistical modeling of fatigue crack growth rate in Inconel alloy 600［J］. International Journal of Fatigue, 2007, 29(5): 931940.

［6］Grigoriev V, Josefsson B, Lind A, et al. A pinloading tension test for evaluation of thinwalled tubular materials［J］. Scripta Metallurgica et Materialia, 1995, 33(1): 109114.

［7］Yagnik S, Ramasubramian N, Grigoriev V, et al. RoundRobin testing of fracture toughness characteristics of thinwalled tubing［J］. Journal of ASTM International, 2008, 5(2): 121.

［8］Grigoriev V, Jakobsson R. Delayed hydrogen cracking velocity and Jintegral measurements on irradiated BWR cladding［J］. ASTM Special Technical Publication, 2006, 1467: 711.

［9］Coleman C, Grigoriev V, Inozemtsev V, et al. Delayed hydride cracking in zircaloy fuel cladding—An IAEA coordinated research programme［J］. Nuclear Engineering and Technology, 2009, 41: 18.

［10］Seok C S, Bae B K, Koo J M. DC potential drop method for evaluating material degradation［J］. KSME International Journal, 2004, 18(8): 13681374.

［11］Bowler N. Theory of fourpoint directcurrent potential drop measurements on a metal plate［J］. Research in Nondestructive Evaluation, 2006, 17(1): 2948.

［12］Merah N. Detecting and measuring flaws using electric potential techniques［J］. Journal of Quality in Maintenance Engineering, 2003, 9(2): 160175.

［13］Andresen P L, Morra M M. IGSCC of nonsensitized stainless steels in high temperature water［J］. Journal of Nuclear Materials, 2008, 383(1): 97111.

［14］Paris P C, Erdogan F. A critical analysis of crack propagation laws［J］. Journal of Basic Engineering, 1963, 85(4): 528533.

［15］ASTM International. Standard Test Method for Measurement of Fatigue Crack Growth Rates［M］. West Conshohocken: ASTM International, 2011.

[1]	王聚团, 戚晓宁, 黄志明. 水下生产管汇测试技术及其改进研究[J]. 海洋工程装备与技术, 2022, 9(2): 43-49.
[2]	袁振钦, 邹科, 孙亚峰, 刘刚, 屈衍, 李居跃. 基于时域分析法的动态电缆疲劳分析[J]. 海洋工程装备与技术, 2022, 9(2): 50-55.
[3]	王娟, 杨明旺, 郑茂尧, 刘凌云, 赵立君. 高强钢在大型半潜式平台组块建造中的应用[J]. 海洋工程装备与技术, 2022, 9(1): 27-31.
[4]	陈欣, 赵晓磊, 王立坤, 肖德明, 张腾月. 深水大型吸力锚建造技术研究[J]. 海洋工程装备与技术, 2022, 9(1): 32-36.
[5]	尹彦坤, 易涤非. 半潜式生产平台船体结构关键节点工程临界评估[J]. 海洋工程装备与技术, 2022, 9(1): 52-57.
[6]	MA Qunsheng (马群圣), CEN Xingxing (岑星星), YUAN Junyi (袁骏毅), HOU Xumin (侯旭敏). Word Embedding Bootstrapped Deep Active Learning Method to Information Extraction on Chinese Electronic Medical Record[J]. J Shanghai Jiaotong Univ Sci, 2021, 26(4): 494-502.
[7]	ZHANG Shengfa (张胜发), TANG Na (唐纳), SHEN Guofeng (沈国峰), WANG Han (王悍), QIAO Shan (乔杉). Universal Software Architecture of Magnetic Resonance-Guided Focused Ultrasound Surgery System and Experimental Study[J]. J Shanghai Jiaotong Univ Sci, 2021, 26(4): 471-481.
[8]	安庆升, 孙立东, 武秋生. 碳纤维增强复合材料发射筒设计研究[J]. 空天防御, 2021, 4(2): 13-.
[9]	KONG Xiangqiang (孔祥强), MENG Xiangxi (孟祥熙), LI Jianbo (李见波), SHANG Yanping (尚燕平), CUI Fulin (崔福林) . Comparative Study on Two-Stage Absorption Refrigeration Systems with Different Working Pairs[J]. J Shanghai Jiaotong Univ Sci, 2021, 26(2): 155-162.
[10]	ZHUANG Weimin (庄蔚敏), WANG Pengyue (王鹏跃), AO Wenhong (熬文宏), CHEN Gang (陈刚) . Experiment and Simulation of Impact Response of Woven CFRP Laminates with Different Stacking Angles[J]. J Shanghai Jiaotong Univ Sci, 2021, 26(2): 218-230.
[11]	ZHOU Xuhui (周旭辉), ZHANG Wenguang (张文光), XIE Jie (谢颉). Effects of Micro-Milling and Laser Engraving on Processing Quality and Implantation Mechanics of PEG-Dexamethasone Coated Neural Probe[J]. J Shanghai Jiaotong Univ Sci, 2021, 26(1): 1-9.
[12]	HUANG Ningning (黄宁宁), MA Yixin (马艺馨), ZHANG Mingzhu (张明珠), GE Hao (葛浩), WU Huawei (吴华伟). Finite Element Modeling of Human Thorax Based on MRI Images for EIT Image Reconstruction[J]. J Shanghai Jiaotong Univ Sci, 2021, 26(1): 33-39.
[13]	WANG Xianjin, GAO Xu, YU Kuigang . Fixture Locating Modelling and Optimization Research of Aluminum Alloy Sidewall in a High-Speed Train Body[J]. J Shanghai Jiaotong Univ Sci, 2020, 25(6): 706-713.
[14]	QIAO Xing, MA Dan, YAO Xuliang, FENG Baolin. Stability and Numerical Analysis of a Standby System[J]. J Shanghai Jiaotong Univ Sci, 2020, 25(6): 769-778.
[15]	WU Jin, MIN Yu, YANG Xiaodie, MA Simin . Micro-Expression Recognition Algorithm Based on Information Entropy Feature[J]. Journal of Shanghai Jiao Tong University(Science), 2020, 25(5): 589-599.