基于双相钢板DP780弯曲试验的模具材料磨损性能

上海交通大学学报（自然版） ›› 2014, Vol. 48 ›› Issue (05): 594-599.

基于双相钢板DP780弯曲试验的模具材料磨损性能

岳懂，孙利，于忠奇

(上海交通大学上海市复杂薄板结构数字化制造重点试验室, 上海 200240)

收稿日期:2013-10-11 出版日期:2014-05-28 发布日期:2014-05-28
基金资助:
国家自然科学基金资助项目(51275298)；上海市自然科学基金资助项目(11ZR1417900)

Wear Characteristics on Tools in U-shaped Stretch-Bending of Dual-Phase Steel Sheet DP780

YUE Dong,SUN Li,YU Zhongqi

(Shanghai Key Laboratory of Digital Manufacture for ThinWalled Structures, Shanghai Jiaotong University, Shanghai 200240, China)

Received:2013-10-11 Online:2014-05-28 Published:2014-05-28

摘要/Abstract

摘要：

采用U形拉伸-弯曲成形试验方法研究了用于先进高强度双相钢裸板DP780的3种模具材料的磨损性能.结果表明：经过热扩散碳化物覆层（TD）处理的模具材料V4E及DC53的耐磨损性最佳；经过真空热处理的模具材料DC53的耐磨性能较差；对于经TD处理的V4E及DC53，模具的磨损主要集中在凹模圆角入口0°~15°区域，而对于真空热处理的DC53，模具在凹模圆角和法兰处均出现了严重的磨损.

关键词: 高强度双相钢, 拉伸-弯曲成形试验, 模具材料, 磨损性能

Abstract:

Finding the most suitable tool material is the main way to reduce the wear on the surface of parts and enhance the life of tools in the advanced high strength steel stamping. This paper investigated the wear resistance and characteristics of different tool materials—V4E(TD), DC53(TD) and DC53(vacuum heat treatment) in U-stretching-bending experiment using DP780.The result shows that the V4E(TD) and DC53(TD) have a good performance on wear resistance, while the DC53 by vacuum heat treatment does not perform well. For the first two inserts, wear mainly occurs in the area of 0°-15°on the die radius. While on the DC53 (vacuum heat treatment), serious wear occurs on both the die radius and flange.

Key words: high strength dual-phase steel, stretch-bending test, tool material, wear characteristic

中图分类号:

TG 386.3

岳懂，孙利，于忠奇. 基于双相钢板DP780弯曲试验的模具材料磨损性能[J]. 上海交通大学学报（自然版）, 2014, 48(05): 594-599.

YUE Dong,SUN Li,YU Zhongqi. Wear Characteristics on Tools in U-shaped Stretch-Bending of Dual-Phase Steel Sheet DP780[J]. Journal of Shanghai Jiaotong University, 2014, 48(05): 594-599.

参考文献

［1］李梅，赵亦希，胡星,等. 先进高强度双相钢汽车板剪切断裂试验［J］. 上海交通大学学报, 2011, 45 (11): 16951699.

LI Mei, ZHAO Yixi, HU Xing, et al. Experimental study of shear fracture on advanced high strength dualphase steels ［J］. Journal of Shanghai Jiaotong University, 2011, 45 (11): 16951699.

［2］Hall J, Mullholland T, Young D. Investigation of stamping tooling durability for dual phase steels ［EB/OL］. ［20131001］. http:∥papers.sae.org/2011011060/.

［3］Kim H, Han S, Yan Q, et al. Evaluation of tool materials, coatings and lubricants in forming of advanced high strength steels (AHSS)［J］. CIRP AnnalsManufacturing Technology, 2008, 57（1）: 299304.

［4］Cora O N, Namiki K, Koc M. Wear performance assessment of alternative stamping die materials utilizing a novel test system ［J］. Wear, 2009, 267(58): 11231129.

［5］Sresomroeng B, Premanond V, Kaewtatip P, et al. Performance of CrN radical nitrided tools on deep drawing of advanced high strength steel ［J］. Surface and Coatings Technology, 2011, 205(1718):41984204.

［6］Kim H, Sung J, Frank E, et al. Investigation of galling in forming galvanized advanced high strength steels (AHSSs) using the twist compression test (TCT)［J］. Journal of Materials Processing Technology, 2008, 205(13): 459468.

［7］Wang W R, Hua M, Wei X C. A comparison study of sliding friction behavior between two high strength DP590 steel sheets against heat treated DC53 punch: Hotdip galvanized sheet versus cold rolled bare sheet ［J］. Tribology International, 2012, 54: 114122.

［8］侯英岢. 汽车钢板冲压成形表面损伤规律与控制方法研究［D］. 上海: 上海交通大学机械与动力工程学院,2009.

［9］照日格图，侯英苛，赵亦希，等. 模具表面形态演化对冲压件表面损伤的影响［J］.上海交通大学学报, 2008, 42(5): 782785.

ZHAO Rigetu, HOU Yingke, ZHAO Yixi, et al. The effect of changing of tool surface microgeometry surface galling in sheet metal ［J］. Journal of Shanghai Jiaotong University, 2008, 42(5): 782785.

［10］Pereira M P, Wenyi Y, Bernard F R. Wear at the die radius in sheet metal stamping ［J］. Wear, 2012, 274275: 355367.

［11］高晶，于忠奇，林忠钦，等. 双相钢板成形界面压力数值仿真及对板料表面损伤影响［J］. 上海交通大学学报， 2013, 47(5): 770774.

GAO Jing, YU Zhongqi, LIN Zhongqin, et al. Numerical analysis for contact pressure and surface damage in dualphase steel sheet stamping ［J］. Journal of Shanghai Jiaotong University, 2013, 47(5): 770774.

［12］温诗铸，黄平. 摩擦学原理［M］. 3版. 北京：清华大学出版社, 2008: 266270.

编辑推荐 0

Metrics

阅读次数

全文

272

HTML			PDF

最新录用	在线预览	正式出版	最新录用	在线预览	正式出版
0	0	0	5	0	267

来源	本网站	其他网站

次数	29	243
比例	11%	89%

摘要

922

最新录用	在线预览	正式出版

54	0	868

来源	本网站	其他网站

次数	349	573
比例	38%	62%

[1]	李星亮1,2，岳文1,3，庞长涛2，徐昌语2，康嘉杰1,3，田斌1,4. 渗氮处理对表面织构化钛在月壤介质中摩擦磨损性能的影响[J]. 上海交通大学学报（自然版）, 2018, 52(5): 561-567.
[2]	何春锋，赵亦希，黄胜. 高强度双相钢板拉弯成形断裂的微观组织形貌分析[J]. 上海交通大学学报（自然版）, 2014, 48(05): 618-623.
[3]	俞亮1，程先华1,2. 改性聚对苯撑苯并双噁唑纤维增强聚酰亚胺复合材料的摩擦磨损性能[J]. 上海交通大学学报（自然版）, 2013, 47(09): 1341-1346.
[4]	方磊1，徐颖1,2，程先华1,3. 钛合金表面稀土碳纳米管薄膜制备及其摩擦磨损性能分析[J]. 上海交通大学学报（自然版）, 2013, 47(05): 740-743.
[5]	谢震，李萌，王武荣，韦习成. 高强度双相钢薄板拉弯成形试验及数值模拟[J]. 上海交通大学学报（自然版）, 2013, 47(05): 760-765.
[6]	单小鹏，郭兴伍，王渠东，丁文江. 镁合金表面MoS2/树脂杂化涂层的制备及其摩擦磨损和电化学性能研究[J]. 上海交通大学学报（自然版）, 2013, 47(05): 822-826.
[7]	张莹1, 胡成亮1, 赵震1, 李爱平2. 冷锻模具材料高速基体钢应变控制室温疲劳性能[J]. 上海交通大学学报（自然版）, 2012, 46(10): 1632-1636.
[8]	李梅，赵亦希，胡星，黄胜. 先进高强度双相钢汽车板剪切断裂实验[J]. 上海交通大学学报（自然版）, 2011, 45(11): 1695-1699.
[9]	李振华1,程先华2. 单晶硅表面有机硅烷/稀土复合自组装膜的摩擦磨损性能[J]. 上海交通大学学报（自然版）, 2011, 45(11): 1577-1580.
[10]	孙志永1, 程先华1, 2. 稀土改性碳纳米管复合薄膜制备及其摩擦磨损性能[J]. 上海交通大学学报（自然版）, 2011, 45(09): 1310-1314.
[11]	徐颖,周华，程先华. MPTS/MPTES复合自组装薄膜的制备及摩擦磨损特性分析 [J]. 上海交通大学学报（自然版）, 2011, 45(01): 83-0087.