Effect Mechanism of Magnetite Aggregates on Electromagnetic Properties and Microwave Absorption Efficiency of Concrete

1.State Key Laboratory for Tunnel Engineering, Shandong University, Jinan 250061, China；2.School of Civil and Environmental Engineering, Zhengzhou University of Aeronautics, Zhengzhou 450046, China；3.School of Materials Science and Engineering, Chang’an University, Xi’an 710061, China

摘要/Abstract

摘要： 为提高混凝土结构的电磁防护能力与微波吸收性能，磁铁矿骨料（MAs）被使用去制备磁铁矿混凝土（MC），通过测定其电磁参数和微波反射损耗（R_loss），并表征其微观结构，建立电磁特性、吸波性能与微观结构之间的构效关系，揭示MAs对MC电磁吸波能力的增强机制。结果表明，MAs通过改善MC的介电性能和磁性能，并影响其孔隙分布和C-S-H凝胶结构，有效提高了MC的电磁损耗能力和阻抗匹配特性，从而增强其吸波能力。与对照组相比，MAs替换率为100 %混凝土的平均R_loss可降低至-7.68 dB，有效带宽可拓宽至7.21 GHz，使其能够宽频范围内将吸波效率提升至80 %以上。

关键词: 磁铁矿骨料, 水泥混凝土, 电磁特性, 微波吸收效率, 微观结构

Abstract:

To enhance the electromagnetic protection and microwave absorption properties of concrete structures, magnetite aggregates (MAs) were used to prepare magnetite concrete (MC). By measuring electromagnetic parameters and microwave reflection loss (R_loss), the electromagnetic absorbing properties of the MC was analyzed, and its microstructures were characterized. By establishing the structure-activity relationship between electromagnetic properties, microwave absorption properties and microstructures, the enhancement mechanism of MAs on the absorbing efficiency of MC was revealed. The results showed that MAs effectively enhance the electromagnetic loss ability and impedance matching characteristics of MC by improving its dielectric and magnetic properties, as well as influencing its pore distribution and C-S-H gel structures. Compared with the control group, the mean R_loss of the concrete with 100 % MAs content reduced to -7.68 dB, and the effective bandwidth expanded to 7.21 GHz, enabling it absorbing microwave efficiency to be more than 80 % at wide frequency range.

Key words: magnetite aggregates, cement concrete, electromagnetic properties, microwave absorption efficiency, microstructure

中图分类号:

TU528

邱贺枰1, 张庆松1, 万赈民2, 陈新1, 陈华鑫3. 磁铁矿骨料对混凝土电磁特性和微波吸收效率的影响机理[J]. 上海交通大学学报, doi: 10.16183/j.cnki.jsjtu.2025.335.

QIU Heping1, ZHANG Qingsong1, WAN Zhenmin2, CHEN Xin1, CHEN Huaxin3.

Effect Mechanism of Magnetite Aggregates on Electromagnetic Properties and Microwave Absorption Efficiency of Concrete [J]. Journal of Shanghai Jiao Tong University, doi: 10.16183/j.cnki.jsjtu.2025.335.

[1]	朱懋江，翁兴中，张俊，杨博瀚，刘军忠. 装配式水泥混凝土道面灌浆层的粘结特性[J]. 上海交通大学学报, 2019, 53(6): 696-703.
[2]	于谦，张文光，尹雪乐. 基于定向电沉积的神经电极表面性能[J]. 上海交通大学学报, 2019, 53(11): 1308-1315.
[3]	宋小勇a, b, 李云飞b, c. 真空预冷处理对洋葱表皮微观结构及性能的影响[J]. 上海交通大学学报（自然版）, 2012, 46(05): 819-824.
[4]	刘畅, 许金泉, 孟祥琦, 李晨. 基于原子力显微镜的薄膜涂层界面观测及其变形特性[J]. 上海交通大学学报（自然版）, 2011, 45(10): 1485-1488.
[5]	杨朝军，张志鹏，廖士光. 证券市场流动性综合测度指标研究[J]. 上海交通大学学报（自然版）, 2008, 42(11): 1767-1771.
[6]	石春香，杨群，郭忠印. 公路隧道水泥混凝土路面设计方法[J]. 上海交通大学学报（自然版）, 2008, 42(11): 1884-1887.