冲裁工艺对无取向电工钢叠片磁性能的影响

doi:10.16183/j.cnki.jsjtu.2019.09.014

摘要/Abstract

摘要： 为研究冲裁工艺对电动机定子铁芯的磁性能影响，采用不同的冲头和冲裁间隙，对无取向电工钢圆片进行冲裁加工，研究在不同冲裁工艺参数下所冲出的电工钢圆环叠片磁性能优劣.通过纳米压痕测试表征了无取向电工钢冲裁边缘的残余应力分布，研究了无取向电工钢磁性能劣化与残余应力分布的关系.结果表明：对比3种不同冲头加工，平冲头冲裁后无取向电工钢叠片磁性能劣化程度最小，凹冲头次之，斜冲头最严重.当冲裁间隙为板厚的5%～20%时，随着冲裁间隙不断增大，无取向电工钢叠片磁性能劣化程度先减小后增大，存在最佳间隙.无取向电工钢叠片的磁性能劣化程度主要与冲裁边缘的残余应力峰值有关，残余应力峰值越大，无取向电工钢叠片磁性能劣化越严重.本研究可为工业无取向电工钢冲裁加工提供参数优化指导.

关键词: 冲裁工艺；无取向电工钢叠片；磁性能测试；残余应力

Abstract: In order to study the influence of blanking process on the magnetic properties of non-oriented electrical steel lamination, different shapes of punch and different blanking clearances are adopted. The relationship between the magnetic property deterioration and residual stress distribution of non-oriented electrical steel is studied. The results show that the blanking performance of the flat punch is the best, and the concave punch is better than the beveled one. In the considered blanking clearance range (5%～20% of sheet thickness), the magnetic property deterioration of the non-oriented electrical steel lamination decreases at first and then increases with the increasing blanking clearance. There exists an optimal clearance for reducing the magnetic properties deterioration. The magnetic property deterioration of non-oriented electrical steel lamination is mainly related to the peak residual stress. The larger the peak residual stress is, the worse the magnetic properties are. The study can provide parameter optimization guidance for blanking process of non-oriented electrical steel in industry.

Key words: blanking process; non-oriented electrical steel lamination; magnetic property tests; residual stress

中图分类号:

TG 386

王心可，汪喆，崔荣高，李淑慧. 冲裁工艺对无取向电工钢叠片磁性能的影响[J]. 上海交通大学学报, 2019, 53(9): 1115-1121.

WANG Xinke，WANG Zhe，CUI Ronggao，LI Shuhui. Influence of Blanking Process on the Magnetic Properties of Non-Oriented Electrical Steel Lamination[J]. Journal of Shanghai Jiaotong University, 2019, 53(9): 1115-1121.

参考文献

［1］何忠治. 电工钢［M］. 北京: 冶金工业出版社, 1997.
HE Zhongzhi. The electrical steel［M］. Beijing: The Metallurgical Industry Press, 1997.
［2］ODA Y, KOHNO M, HONDA A. Recent development of non-oriented electrical steel sheet for automobile electrical devices［J］. Journal of Magnetism and Magnetic Materials, 2008, 320: 2430-2435.
［3］NAKAZAKI O, KAI Y, TODAKA T, et al. Iron loss properties of a practical rotating machine stator core at each manufacturing stage［J］. Journal of Magnetism and Magnetic Materials, 2010, 33: 79-86.
［4］韩志磊, 胡树兵, 熊雪松, 等. 冲剪加工对无取向硅钢边缘组织和磁性能的影响［J］. 材料热处理学报, 2014, 35(Sup.): 154-158.
HAN Zhilei, HU Shubing, XIONG Xuesong, et al. Influence of punching process on microstructure near cutting edge and magnetic properties of non-oriented electrical steel［J］. Transactions of Materials and Heat Treatment, 2014, 35(Sup.): 154-158.
［5］WEISS H A, LEUNING N, STEENTJES S, et al. Influence of shear cutting parameters on the electromagnetic properties of non-oriented electrical steel sheets［J］. Journal of Magnetism and Magnetic Materials, 2017, 421: 250-259.
［6］HOLOPAINEN T P, RASILO P, ARKKIO A. Identification of magnetic properties for cutting edge of electrical steel sheets［J］. IEEE Transactions on Industry Applications, 2012, 53(2): 1049-1053.
［7］MAUREL V, OSSART B, BILLARDON R. Resi-dual stresses in punched laminations: Phenomenological analysis and influence on the magnetic behavior of electrical steels［J］. Journal of Applied Physics, 2003, 93(10): 7106-7108.
［8］CAO H, HAO L, YI J, et al. The influence of pun-ching process on residual stress and magnetic domain structure of non-oriented silicon steel［J］. Journal of Magnetism and Magnetic Materials, 2016, 406: 42-47.
［9］NAKATA T, NAKANO M, KAWAHARA K. Effects of stress due to cutting on magnetic characte-ristics of silicon steel［J］. IEEE Translation Journal on Magnetics in Japan, 1992, 7(6): 453-457.
［10］ZHU L N, XU B S, WANG H D, et al. Measurement of residual stress in quenched 1045 steel by the nanoindentation method［J］. Materials Characterization, 2010, 61(12): 1359-1362.
［11］王洪泽. 电工钢叠片激光焊接界面传热行为与磁性能劣化机理研究［D］. 上海: 上海交通大学, 2016.
WANG Hongze. Study on interfacial heat transfer in laser welding of laminated electrical steels and magnetic properties degradation［D］ Shanghai: Shanghai Jiao Tong University, 2016.
［12］郭钊, 唐文亭, 曹立勋. 圆管异形孔冲裁工艺设计及有限元模拟［J］. 锻压技术, 2014, 39(8): 140-145.
GUO Zhao, TANG Wenting, CAO Lixun. Process design and numerical simulation on shaped hole blanking of steel round pipe［J］. Forging & Stamping Technology, 2014, 39(8): 140-145.
［13］曹洪志, 郝林坡, 吴维, 等.模具间隙对无取向硅钢冲片质量的影响研究［J］. 锻压技术, 2016, 41(3): 94-98
CAO Hongzhi, HAO Linpo, WU Wei, et al. Research on influence of die clearance on the quality of non-oriented electrical steel parts［J］. Forging & Stamping Technology, 2016, 41(3): 94-98.
［14］HARSTICK H M S, RITTER M, RIEHEMANN W. Influence of punching and tool wear on the magnetic properties of nonoriented electrical steel［J］. IEEE Transactions of Magnetics, 2014, 50(4): 69-73.
［15］WANG H Z, ZHANG Y S, LI S H. Laser welding of laminated electrical steels［J］. Journal of Materials Processing Technology, 2016, 230: 99-108.

编辑推荐 0

Metrics

阅读次数

全文

489

HTML			PDF

最新录用	在线预览	正式出版	最新录用	在线预览	正式出版
0	0	0	0	0	489

来源	本网站	其他网站

次数	304	185
比例	62%	38%

摘要

1276

最新录用	在线预览	正式出版

0	0	1276

来源	本网站	其他网站

次数	682	594
比例	53%	47%

[1]	刘永财，鲍益东，秦雪娇，刘玉琳，陈文亮. 板料成形快速模拟的中间构形构造方法[J]. 上海交通大学学报, 2019, 53(6): 713-718.
[2]	詹杨，赵亦希，朱宝行. 铝合金车身窗框亮条翻边圆角不均匀缺陷解决方案[J]. 上海交通大学学报（自然版）, 2019, 53(4): 488-496.
[3]	刘若凡, 于忠奇, 赵亦希, EVSYUKOV S A. 法兰约束条件下铝合金杯形件的旋压成形性能[J]. 上海交通大学学报, 2019, 53(1): 105-110.
[4]	李东玮, 王磊, 张聪, 赵亦希. 预折刀工作终止位置对包边边界缩进的影响[J]. 上海交通大学学报, 2019, 53(1): 100-104.
[5]	晏佳伟，胡启，王振振，陈军. 不同硬化模型对第3代超高强度钢板冲压回弹预测的比较[J]. 上海交通大学学报（自然版）, 2017, 51(11): 1334-1339.
[6]	顾新建，于忠奇，宋洋. 工艺参数对高强度钢冷冲压界面温度影响分析[J]. 上海交通大学学报（自然版）, 2017, 51(4): 426-.
[7]	郑先坤，王武荣，韦习成. 热镀锌先进高强度钢板摩擦耦合塑性变形行为[J]. 上海交通大学学报（自然版）, 2017, 51(4): 432-.
[8]	阎昱，王海波，赵溦. 与应变速率相关的DP980高强度钢板辊弯成形的本构模型建立[J]. 上海交通大学学报（自然版）, 2015, 49(01): 7-11.
[9]	岳懂，孙利，于忠奇. 基于双相钢板DP780弯曲试验的模具材料磨损性能[J]. 上海交通大学学报（自然版）, 2014, 48(05): 594-599.
[10]	宋修成，陆彬，陈军. 基于预拉伸与数控渐进成形复合的轿车翼子板样件制造技术[J]. 上海交通大学学报（自然版）, 2013, 47(05): 754-759.
[11]	高晶1，刘克素2，于忠奇1，林忠钦1. 双相钢板成形界面压力数值仿真及对板料表面损伤影响[J]. 上海交通大学学报（自然版）, 2013, 47(05): 770-774.
[12]	卢健，陈军，张飞飞，陈劼实. 基于三维Hill’48屈服准则的液压成形本构模型及数值验证[J]. 上海交通大学学报（自然版）, 2013, 47(05): 791-794.
[13]	周国伟a, 李大永a, b, 彭颖红a, b. 7075-T6高强度铝合金温热条件下的拉深成形性能[J]. 上海交通大学学报（自然版）, 2012, 46(09): 1482-1486.
[14]	张骥超1, 刘罡2, 林忠钦1, 高伟3, 李淑慧1. 侧围外板冲压工艺稳健性优化设计[J]. 上海交通大学学报（自然版）, 2012, 46(07): 1005-1010.
[15]	付泽民, 张而耕, 刘旭辉, 胡大超. 板材多道次渐进折弯成形回弹补偿的模具修正 [J]. 上海交通大学学报（自然版）, 2012, 46(07): 1069-1073.