等径角挤压工艺对Ti5553合金冲蚀磨损性能的影响

摘要/Abstract

摘要：

摘要：考察了经等径角挤压（ECAE）处理前后的Ti5553合金在含泥沙海水环境中的冲蚀磨损特性，采用扫描电子显微镜观察冲蚀磨损后的试样表面形貌并结合MATLAB软件进行定量分析，探讨了Ti5553合金显微组织、力学性能及冲蚀机理的演变对其冲蚀磨损性能的影响.结果表明：经ECAE处理后，Ti5553合金的抗冲蚀磨损性能明显提高，这是由于ECAE工艺能够通过细晶强化而提高Ti5553合金的强度与韧塑性、改善其微观组织所致；未经ECAE处理的Ti5553合金的冲蚀磨损机理为冲击变形及犁沟剥落，并伴随大面积划痕和冲击坑裂纹的产生，而经ECAE处理的Ti5553合金的冲蚀机理为轻微冲击变形及犁沟剥落，划痕和冲击坑裂纹的扩展趋势不明显.

关键词: Ti5553钛合金, 等径角挤压, 冲蚀磨损, 表面形貌, 灰度

Abstract:

Abstract： A novel method was proposed to improve the erosion wear behaviour of Ti5553 exposed to seawater with quartzes, in which the erosion performance of Ti5553 treated by equal channel angular extrusion (ECAE) was compared with that of counterpart without ECAE treatment. The results indicate that the sample treated by ECAE demonstrates a significantly improved erosion wear resistance due to the grain refinement introduced by ECAE, resulting in the improvement of tensile strength, ductility, toughness and microstructure of the sample. Scanning electron microscope (SEM), assisted by quantitative analysis utilising Matlab, was adopted to generate the surface morphology of the samples. With the exploration of the microstructure, mechanical properties and erosion mechanism evolution dependence of erosion wear behaviour, it is found that the erosion mechanism of the sample treated by ECAE has impact deformation and ploughing, accompanied by severe scratching and crater cracks while that of the sample without ECAE treatment has slight impact deformation and ploughing, with shallow scratching and crater cracks.
Key words：

Key words: titanium alloy Ti5553, equal channel angular extrusion (ECAE), erosion wear, surface morphology, gray scale

中图分类号:

TG 146

李振华1，马彩云1,华晨2，程先华2,3. 等径角挤压工艺对Ti5553合金冲蚀磨损性能的影响[J]. 上海交通大学学报（自然版）, 2015, 49(01): 37-43.

LI Zhenhua1,MA Caiyun1,HUA Chen2,CHENG Xianhua2,3. Influence of Equal Channel Angular Extrusion on Erosion Wear Resistance of Ti5553[J]. Journal of Shanghai Jiaotong University, 2015, 49(01): 37-43.

参考文献

［1］Jones N G，Dashwood R J，Jackson M, et al. Beta phase decomposition in Ti5Al5Mo5V3Cr［J］. Acta Mater，2009，57(13)：38303839.

［2］Jones N G，Dashwood R J，Dye D, et al. The flow behavior and microstructural evolution of Ti5Al5Mo5V3Cr during subtransus isothermal forging［J］. Metall Mater Trans A, 2009, 40(8): 19441954.

［3］李振华. 等径弯角挤压法制备的钛镍基合金的摩擦学性能研究［D］. 上海: 上海交通大学机械与动力工程学院，2007.

［4］Kleis I，Kulu P. Solid particle erosion［M］. London: Springer, 2008.

［5］Chauhan A K，Goel D B，Prakash S. Solid particle erosion behavior of 13Cr4Ni and 21Cr4NiN steels［J］. J Alloy Compd，2009，467(12)：459464.

［6］郝贠洪，李永. 风沙环境下钢结构涂层低角度冲蚀特性研究［J］. 摩擦学学报，2013，33(4)：343348.

HAO Yunhong，LI Yong. Erosionbehaviors of the coating on steel structure eroded at low erosionangle in sandstorm ［J］. Tribology，2013，33(4)：343348.

［7］刘家浚. 材料磨损原理及其耐磨性［M］. 北京: 清华大学出版社, 1993.

［8］Langdon T G. The principles of grain refinement in equalchannel angular pressing［J］. Materials Science and Engineering A, 2007, 462(12): 311.

［9］Ferrasse S，Segal V M，Alford F, et al. Scale up and application of equalchannel angular extrusion for the electronics and aerospace industries［J］. Materials Science and Engineering A, 2008, 493(12): 130140.

［10］Beyerlein I J, Field R D, Hartwig K T, et al. Texture development in twopass ecaeprocessed beryllium［J］. J Mater Sci, 2008, 43(2324): 74657473.

［11］梁工英，杨琛，苏俊义. 激光表面处理对球墨铸铁冲蚀性能的影响［J］. 摩擦学学报, 2000, 20(2): 115118.

LIANG Gongying，YANG Chen，SU Junyi. The effect of laser surface melting treatment on the erosioncorrosion behaviors of nodular graphite cast iron ［J］. Tribology, 2000, 20(2): 115118.

［12］ASTM G37—2010, Standard test method for liquid impingement erosion using rotating apparatus［S］. USA: ASTM International, 2010.

［13］Liu B，Fang Z B，Wang H B, et al. Effect of cross linking degree and adhesion force on the anticorrosion performance of epoxy coatings under simulated deep sea environment［J］. Progress in Organic Coatings, 2013, 76(12): 18141818.

［14］Yang Y G，Zhang T，Shao Y W, et al. New understanding of the effect of hydrostatic pressure on the corrosion of NiCrMoV high strength steel［J］. Corrosion Science, 2013, 73: 250261.

［15］Shan L，Wang Y X，Li J L, et al. Tribological behaviors of PVD TiN and TiCN coatings in artificial seawater［J］. Surface and Coatings Technology, 2013, 226: 4050.

［16］Dua A K. Principles and applications of SEM and EDAX ［J］. Materials Science Foundations, 2009, 951: 495513.

［17］Waits C M，Modafe A，Ghodssi R. Investigation of grayscale technology for large area 3D silicon mems structures［J］. J Micromech Microeng, 2003, 13(2): 170177.

［18］Goldstein J，Newbury D E，Joy D C, et al. Scanning electron microscopy and Xray microanalysis［M］. New York: Plenum Press, 2003.

[1]	练鹏, 杨积东, 叶宋杭, 占晓敏. 一种基于星图灰度分布特征的星敏感器质量分类方法[J]. 空天防御, 2025, 8(2): 118-124.
[2]	胡锦昊, 王明昊, 夏天扬, 王悦行, 杜海静, 徐传刚. 基于HSV色彩空间的红外与可见光图像融合方法[J]. 空天防御, 2021, 4(4): 87-94.
[3]	张燕, 贾振宇, 周顾人, 黄峥嵘, 刘静秋. 基于多方向混合模板的红外弱小目标检测算法[J]. 空天防御, 2019, 2(1): 64-69.
[4]	陈实1，张执南1，蔡晓江2，魏新生2. 磨削参数对工件表面形貌及其摩擦性能的影响[J]. 上海交通大学学报（自然版）, 2018, 52(5): 575-581.
[5]	唐鸿远a，张臻b,c，邓运来a,b,c,叶凌英a，钱鹏伟b,c，赵龙a. 基于灰色系统理论的Al-Zn-Mg合金板材疲劳寿命预测[J]. 上海交通大学学报（自然版）, 2018, 52(2): 228-232.
[6]	蒋华军a，蔡艳a,b，李超豪a，李芳a,b，华学明a,b. 基于改进Sobel算法的焊缝X射线图像气孔识别方法[J]. 上海交通大学学报（自然版）, 2017, 51(6): 665-671.
[7]	万磊, 曾文静, 秦再白, 黄蜀玲. 海面目标自适应实时检测 [J]. 上海交通大学学报（自然版）, 2012, 46(09): 1421-1427.
[8]	陈古春a, 苏波b, 王士林b, 李生红a. 基于图片DCT域共生矩阵的图像拼接盲检测[J]. 上海交通大学学报（自然版）, 2011, 45(10): 1547-1551.