金属表面涂覆干燥剂的防凝露研究

摘要/Abstract

摘要：

摘要：针对金属设备表面发生凝露问题，提出在金属表面涂覆硅胶干燥剂的技术方案，通过硅胶被动吸湿防止凝露产生.通过构建实验系统，用发生凝露的时间参数t表征此措施的防凝露效果.实验表明，涂覆硅胶干燥剂可延长t，当金属温度低于露点温度时，对应环境的露点温度越低，防凝露效果越好；当露点温度一定时，金属温度越高，防凝露效果越明显.进一步用吸附动力学模型对涂覆干燥剂金属样片的凝露过程进行分析，并计算了水蒸气扩散系数，其大小影响凝露发生的时间.结果表明，扩散系数与环境的水蒸气分压及硅胶自身温度有关.当硅胶温度相同时，水蒸气分压越小，扩散系数越小；当水蒸气分压相同时，硅胶温度越高，扩散系数越小，发生凝露所需时间越长.

关键词: 金属表面, 硅胶, 凝露, 动态吸湿

Abstract:

Abstract： Water vaporcondensation on metal surface causes corrosion and further affects the performance. In order to decrease this disadvantageous effect, in this paper, the coating of desiccant material (silica gel) to metal surface was proposed. The performance of this method was analyzed both by experiments and by theoretical investigation. Condensation time was adopted as the performance index. Experimental results indicate that desiccantcoated metal surface can effectively delay condensation time which is defined as parameter t. When the temperature difference between metal surface and the dew point is constant, t increases with the decrease of the dew point temperature.When the dew point temperature is constant, t increases with the increase of metal surface temperature. Then, the dynamic condensation process on metal surface was analyzed using the adsorption kinetic model. The diffusivity of water vapor is calculated, because t is affected by the diffusivity of water. The results show that the diffusivity of water vapor is affected significantly by the temperature of silica gel and the water vapor partial pressure. When the temperature of silica is constant, the water vapor diffusivity decreases with decreasing water vapor partial pressure. And when the water vapor partial pressure is constant, the water diffusivity decreases with decreasing temperature of silica, leading to a longer delay time of condensation.
Key words：

Key words: metal surface, silica, condensation, adsorption kinetics

中图分类号:

TQ 021.4

郝瑞英，葛天舒，代彦军. 金属表面涂覆干燥剂的防凝露研究[J]. 上海交通大学学报（自然版）, 2014, 48(11): 1588-1594.

HAO Ruiying,GE Tianshu,DAI Yanjun. Anti-Condensation Based on DesiccantCoated Metal Surface[J]. Journal of Shanghai Jiaotong University, 2014, 48(11): 1588-1594.

参考文献

［1］郑松, 宣永梅, 王海亮. 辐射供冷系统结露问题的研究现状［J］. 制冷与空调(四川), 2012, 26(4): 022.

ZHENG Song, XUAN Yongmei, WANG Hailiang. Current research of radiant cooling condensation［J］. Refrigeration and Air Conditioning(Sichuan), 2012, 26(4): 022.

［2］周敏锐. 冷辐射围护结构表面结露特性与热环境研究［D］. 长沙：湖南大学, 2010.

［3］李欧卿, 魏芃,朱箭. 室外通讯机柜防结露研究［J］. 电子机械工程, 2011, 27(5): 14.

LI Ouqing, WEI Peng, ZHU Jian. Study on condensation prevention of outdoor telecom cabinet［J］.ElectroMechanical Engineering, 2011, 27(5): 14.

［4］房志勇,秘立环. 寒冷地区通信机房内部结露可能性分析［J］. 墙材革新与建筑节能, 2010(008): 4547.

FANG Zhiyong, MI Lihuan. Analysis on the possibility of condensation inside telecom cabinet in cold areas［J］. Wall Materials Innovation and Energy Saving in Buildings, 2010(008): 4547.

［5］曹国荣,赵燕峰. 变频器的除湿防凝露研究［J］. 变频器世界, 2011(6): 129132.

CAO Guorong, ZHAO Yanfeng. Research on the dehumidification and anticondensation in the inverter［J］. The World of Inverters, 2011(6): 129132.

［6］Tencer M, Moss J S. Humidity management of outdoor electronic equipment: methods, pitfalls, and recommendations［J］.Components and Packaging Technologies, IEEE Transactions on, 2002, 25(1): 6672.

［7］ZHANG Yafang. Experimental and CFD evaluation of humidity management methods of ruggedizinga COTS electronics system for a severe climatic environment［D］. Hgskolani Jnkping：JTH,2007.

［8］孙玉玉, 王凤车, 刑征锦, 等. 温湿度试验中结露的产生与预防措施探讨［J］. 环境技术, 2008(6): 1114.

SUN Yuyu, WANG Fengche, XING Zhengjin,et al. Research on the formation of dew and preventive measures in the temperaturehumidity test［J］. Environmental Technology,2008(6): 1114.

［9］郑万兵. 室内游泳池围护结构结露机理与预防措施［J］. 工业安全与环保, 2004, 30(1): 3840.

ZHENG Wanbing. Dew producing mechanism for surrounding structure in indoor swimming pool and its preventive measures［J］. Industrial Safety and Environmental Protection,2004, 30(1): 3840.

［10］La D, Dai Y J, Li Y, et al. Technical development of rotary desiccant dehumidification and air conditioning: a review［J］. Renewable and Sustainable Energy Reviews, 2010, 14(1): 130147.

［11］彭作战. 再生式除湿换热器除湿性能研究［D］. 上海: 上海交通大学, 2010.

［12］冉茂宇. 封闭空间调湿材料新的调湿特性指标及其理论基础［J］. 华侨大学学报: 自然科学版, 2003, 24(1): 6469.

RAN Maoyu. A new characteristic index BT of the humidity controlling material in a closed space and its theoretical basis［J］.Journal of Huaqiao University:Natural Science, 2003, 24(1): 6469.

［13］郑树伟, 丘林, 王文海. 调湿建材应用于辐射供冷房间的可行性［J］. 制冷与空调, 2004, 4(4): 7073.

ZHENG Shuwei, QIU Lin, WANG Wenhai. The feasibility analysis of applying moisture—Condition material to the radiant cooling room［J］. Refrigeration and AirConditioning，2004, 4(4): 7073.

［14］Dai Y J. Production method of regenerative desiccant heat exchanger［P］. China: CN101464075, 20090624.

［15］刘业凤, 王如竹. 新型复合吸附干燥剂的吸附动力学特性研究［J］. 上海理工大学学报，2006,28(2):107110.

LIU Yefeng, WANG Ruzhu. Study on adsorption kinetics characteristic of a kind of new composite desiccant［J］. Journal of University of Shanghai for Science and Technology, 2006,28(2):107110.

［16］Aristov Y I, Tokarev M M, Freni A, et al. Kinetics of water adsorption on silica Fuji Davison RD［J］. Microporous and Mesoporous Materials, 2006, 96(1): 6571.

［17］Boyd G E, Adamson A W, Myers Jr L S. The exchange adsorption of ions from aqueous solutions by organic zeolites II kinetics1 ［J］. Journal of the American Chemical Society, 1947, 69(11): 28362848.

［18］Malash G F, ElKhaiary M I. Piecewise linear regression: A statistical method for the analysis of experimental adsorption data by the intraparticlediffusion models［J］. Chemical Engineering Journal, 2010, 163(3): 256263.

［19］(美)J 赛克利，埃文斯，索恩，等.气固反应［M］. 胡道和译. 北京:中国建筑工业出版社, 1986.

[1]	彭佳杰, 潘权稳, 葛天舒, 王如竹. 太阳能热驱动的吸附式冷热联供系统性能测试[J]. 上海交通大学学报, 2020, 54(7): 661-667.
[2]	樊聪，胡广洪，凌成智. 聚合物-金属直接成型技术[J]. 上海交通大学学报（自然版）, 2018, 52(2): 176-181.